TiO2 nanoparticles functionalized by Pd nanoparticles for gas-sensing application with enhanced butane response performances.

ABSTRACT: Pd functionalized TiO2 nanoparticles were synthesized by a facile hydrothermal method. The structure, morphology, surface chemical states and surface area were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), and N2 adsorption-desorption isotherms, respectively. The as-synthesized pure and Pd functionalized TiO2 nanoparticles were used to fabricate indirect-heating gas sensor, and the gas-sensing characteristics towards butane were investigated. At the optimum temperature, the sensors possess good response, selectivity, response/recovery, repeatability as well as long-term stability. Especially for the high response, the response of 7.5 mol% Pd functionalized TiO2 nanoparticles based sensor reaches 33.93 towards 3000 ppm butane, which is about 9 times higher than that of pure TiO2 nanoparticles. The response and recovery time are 13 and 8 s, respectively. Those values demonstrate the potential of using as-synthesized Pd functionalized TiO2 nanoparticles as butane gas detection, particularly in the dynamic monitoring. Apart from these, a possible mechanism related to the enhanced sensing performance is also investigated.

SUBMITTER: Chen N

PROVIDER: S-EPMC5550448 | biostudies-other | 2017 Aug

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Pd-Functionalized SnO₂ Nanofibers Prepared by Shaddock Peels as Bio-Templates for High Gas Sensing Performance toward Butane.

Project description:Pd-functionalized one-dimensional (1D) SnO₂ nanostructures were synthesized via a facile hydrothermal method and shaddock peels were used as bio-templates to induce a 1D-fiber-like morphology into the gas sensing materials. The gas-sensing performances of sensors based on different ratios of Pd-functionalized SnO₂ composites were measured. All results indicate that the sensor based on 5 mol % Pd-functionalized SnO₂ composites exhibited significantly enhanced gas-sensing performances toward butane. With regard to pure SnO₂, enhanced levels of gas response and selectivity were observed. With 5 mol % Pd-functionalized SnO₂ composites, detection limits as low as 10 ppm with responses of 1.38 ± 0.26 were attained. Additionally, the sensor exhibited rapid response/recovery times (3.20/6.28 s) at 3000 ppm butane, good repeatability and long-term stability, demonstrating their potential in practical applications. The excellent gas-sensing performances are attributed to the unique one-dimensional morphology and the large internal surface area of sensing materials afforded using bio-templates, which provide more active sites for the reaction between butane molecules and adsorbed oxygen ions. The catalysis and "spillover effect" of Pd nanoparticles also play an important role in the sensing of butane gas as further discussed in the paper.

| S-EPMC6359564 | biostudies-literature

SnO2 Nanoparticles–CeO2 Nanorods Enriched with Oxygen Vacancies for Bifunctional Sensing Performances toward Toxic CO Gas and Arsenate Ions

Project description:In this paper, we

| S-EPMC9201895 | biostudies-literature

Room-temperature ammonia gas sensing via Au nanoparticle-decorated TiO2 nanosheets

Project description:A high-performance gas sensor operating at room temperature is always favourable since it simplifies the device fabrication and lowers the operating power by eliminating a heater. Herein, we fabricated the ammonia (NH3) gas sensor by using Au nanoparticle-decorated TiO2 nanosheets, which were synthesized via two distinct processes: (1) preparation of monolayer TiO2 nanosheets through flux growth and a subsequent chemical exfoliation and (2) decoration of Au nanoparticles on the TiO2 nanosheets via hydrothermal method. Based on the morphological, compositional, crystallographic, and surface characteristics of this low-dimensional nano-heterostructured material, its temperature- and concentration-dependent NH3 gas-sensing properties were investigated. A high response of ~ 2.8 was obtained at room temperature under 20 ppm NH3 gas concentration by decorating Au nanoparticles onto the surface of TiO2 nanosheets, which generated oxygen defects and induced spillover effect as well. Supplementary Information The online version contains supplementary material available at 10.1186/s11671-023-03798-5.

| S-EPMC10214923 | biostudies-literature

Functionalized TiO2 nanoparticles labelled with 225Ac for targeted alpha radionuclide therapy.

Project description:The 225Ac radioisotope exhibits very attractive nuclear properties for application in radionuclide therapy. Unfortunately, the major challenge for radioconjugates labelled with 225Ac is that traditional chelating moieties are unable to sequester the radioactive daughters in the bioconjugate which is critical to minimize toxicity to healthy, non-targeted tissues. In the present work, we propose to apply TiO2 nanoparticles (NPs) as carrier for 225Ac and its decay products. The surface of TiO2 nanoparticles with 25 nm diameter was modified with Substance P (5-11), a peptide fragment which targets NK1 receptors on the glioma cells, through the silan-PEG-NHS linker. Nanoparticles functionalized with Substance P (5-11) were synthesized with high yield in a two-step procedure, and the products were characterized by transmission electron microscopy (TEM), dynamic light scattering (DLS) and thermogravimetric analysis (TGA). The obtained results show that one TiO2-bioconjugate nanoparticle contains in average 80 peptide molecules on its surface. The synthesized TiO2-PEG-SP(5-11) conjugates were labelled with 225Ac by ion-exchange reaction on hydroxyl (OH) functional groups on the TiO2 surface. The labelled bioconjugates almost quantitatively retain 225Ac in phosphate-buffered saline (PBS), physiological salt and cerebrospinal fluid (CSF) for up to 10 days. The leaching of 221Fr, a first decay daughter of 225Ac, in an amount of 30% was observed only in CSF after 10 days. The synthesized 225Ac-TiO2-PEG-SP(5-11) has shown high cytotoxic effect in vitro in T98G glioma cells; therefore, it is a promising new radioconjugate for targeted radionuclide therapy of brain tumours.

| S-EPMC5861168 | biostudies-literature

The Functionalized Single-Walled Carbon Nanotubes Gas Sensor With Pd Nanoparticles for Hydrogen Detection in the High-Voltage Transformers.

Project description:Single-walled carbon nanotubes (SWCNTs) have been widely discussed and applied as novel gas sensing nanomaterials. Hydrogen is one of the remarkable fault characteristic gases in high-voltage oil-paper insulated transformers. In this paper, 3.07 wt% Pd nanoparticles (NPs) were used to decorate SWCNTs. The unloaded, the carboxylated, and the Pd-doped SWCNTs were fabricated into three planar gas sensors, and their gas sensing properties to hydrogen were studied. Gas sensing mechanism was analyzed. Results show that the optimal operating temperature of a Pd-doped SWCNTs-based gas sensor is 125°C lower than that of the unloaded SWCNTs-based gas sensor, and it shows the highest gas sensing response value. This is attributed to the decreasing work function of Pd, which reduces the hole carries in the nanotubes.

| S-EPMC7154150 | biostudies-literature

ppb-Level Selective Hydrogen Gas Detection of Pd-Functionalized In2O3-Loaded ZnO Nanofiber Gas Sensors.

Project description:Pd nanoparticle-functionalized, xIn2O3 (x = 0.05, 0.1, and 0.15)-loaded ZnO nanofibers were synthesized by an electrospinning and ultraviolet (UV) irradiation method and assessed for their hydrogen gas sensing properties. Morphological and chemical analyses revealed the desired morphology and chemical composition of the synthesized nanofibers. The optimal gas sensor namely Pd-functionalized, 0.1In2O3-loaded ZnO nanofibers showed a very strong response to 172-50 ppb hydrogen gas at 350 °C, which is regarded as the optimal sensing temperature. Furthermore, the gas sensors showed excellent selectivity to hydrogen gas due to the much lower response to CO and NO2 gases. The enhanced gas response was attributed to the excellent catalytic activity of Pd to hydrogen gas, and the formation of Pd/ZnO and In2O3/ZnO heterojunctions, ZnO-ZnO homojunction, as well as the formation of PdHx. Overall, highly sensitive and selective hydrogen gas sensors can be produced based on a simple methodology using a synergistic effect from Pd functionalization and In2O3 loading in ZnO nanofibers.

| S-EPMC6806323 | biostudies-literature

Attraction in Action: Reduction of Water to Dihydrogen Using Surface-Functionalized TiO2 Nanoparticles.

Project description:The reactivity of a heterogeneous rhodium(III) and ruthenium(II) complex-functionalized TiO2 nanoparticle (NP) system is reported. The ruthenium and rhodium metal complexes work in tandem on the TiO2 NPs surface to generate H2 through water reduction under simulated and normal sunlight irradiation. The functionalized TiO2 NPs outperformed previously reported homogeneous systems in turnover number (TON) and frequency (TOF). The influence of individual components within the system, such as pH, additive, and catalyst, were tested. The NP material was characterized using TGA-MS, 1H NMR spectroscopy, FTIR spectroscopy, solid absorption spectroscopy, and ICP-MS. Gas chromatography was used to determine the reaction kinetics and recyclability of the NP-supported photocatalyst.

| S-EPMC8912096 | biostudies-literature

Enhanced Dispersion of TiO2 Nanoparticles in a TiO2/PEDOT:PSS Hybrid Nanocomposite via Plasma-Liquid Interactions.

Project description:A facile method to synthesize a TiO2/PEDOT:PSS hybrid nanocomposite material in aqueous solution through direct current (DC) plasma processing at atmospheric pressure and room temperature has been demonstrated. The dispersion of the TiO2 nanoparticles is enhanced and TiO2/polymer hybrid nanoparticles with a distinct core shell structure have been obtained. Increased electrical conductivity was observed for the plasma treated TiO2/PEDOT:PSS nanocomposite. The improvement in nanocomposite properties is due to the enhanced dispersion and stability in liquid polymer of microplasma treated TiO2 nanoparticles. Both plasma induced surface charge and nanoparticle surface termination with specific plasma chemical species are proposed to provide an enhanced barrier to nanoparticle agglomeration and promote nanoparticle-polymer binding.

| S-EPMC4620561 | biostudies-literature

Hybrid Noble-Metals/Metal-Oxide Bifunctional Nano-Heterostructure Displaying Outperforming Gas-Sensing and Photochromic Performances.

Project description:As nanomaterials are dominating 21st century's scene, multiple functionality in a single (nano)structure is becoming very appealing. Inspired by the Land of the Rising Sun, we designed a bifunctional (gas-sensor/photochromic) nanomaterial, made with TiO2 whose surface was simultaneously decorated with copper and silver (the Cu/Ag molar ratio being 3:1). This nanomaterial outperformed previous state-of-the-art TiO2-based sensors for the detection of acetone, as well as the Cu-TiO2-based photochromic material. It indeed possessed splendid sensitivity toward acetone (detection limit of 100 ppb, 5 times lower than previous state-of-the-art TiO2-based acetone sensors), as well as reduced response/recovery times at very low working temperature, 150 °C, for acetone sensing. Still, the same material showed itself to be able to (reversibly) change in color when stimulated by both UV-A and, most remarkably, visible light. Indeed, the visible-light photochromic performance was almost 3 times faster compared to the standard Cu-TiO2 photochromic material-that is, 4.0 min versus 10.8 min, respectively. It was eventually proposed that the photochromic behavior was triggered by different mechanisms, depending on the light source used.

| S-EPMC6644435 | biostudies-literature

Functionalized Nanoparticles for the Dispersion of Gas Hydrates in Slurry Flow.

Project description:Gas hydrates are crystals that can form in oil and gas production. Their agglomeration in flowlines may disrupt the normal production. One current strategy of hydrate management is to inject an anti-agglomerant, a type of low-dosage hydrate inhibitor that prevents hydrate agglomeration. Concerns in the use of these chemicals include their toxicity, cost, and environmental impacts. In this study, we exploited functionalized nanoparticles in place of anti-agglomerants to produce hydrate slurry, with the potential benefit of nanoparticles to be more environmentally friendly and conveniently recyclable. We coated 256 nm spherical silica nanoparticles with different hydrophobicity and evaluated their performance for the hydrate dispersion at atmospheric and high pressure. Nanoparticles with moderate hydrophobicity stabilized oil-in-water (O/W) or water-in-oil (W/O) emulsions. Direct visualization of the cyclopentane hydrate formation from the nanoparticle-stabilized emulsions revealed different morphologies of hydrate particles depending on whether the nanoparticles prevented agglomeration. We also measured the apparent viscosity of a hydrate-nanoparticle mixture using a high-pressure rheometer. Nanoparticles with moderate hydrophobicity during hydrate formation slowed the viscosification, reduced the maximum viscosity, increased the water conversion, and ultimately helped to maintain a low steady-state viscosity. Increasing nanoparticle or salt concentrations also improved the gas hydrate dispersion. Our study demonstrated the great potential of using nanoparticles in preventing agglomeration of gas hydrates under realistic pipeline flow conditions.

| S-EPMC6705207 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data