Cellulose Fibre-Reinforced Biofoam for Structural Applications.

ABSTRACT: Traditionally, polymers and macromolecular components used in the foam industry are mostly derived from petroleum. The current transition to a bio-economy creates demand for the use of more renewable feedstocks. Soybean oil is a vegetable oil, composed mainly of triglycerides, that is suitable material for foam production. In this study, acrylated epoxidized soybean oil and variable amounts of cellulose fibres were used in the production of bio-based foam. The developed macroporous bio-based architectures were characterised by several techniques, including porosity measurements, nanoindentation testing, scanning electron microscopy, and thermogravimetric analysis. It was found that the introduction of cellulose fibres during the foaming process was necessary to create the three-dimensional polymer foams. Using cellulose fibres has potential as a foam stabiliser because it obstructs the drainage of liquid from the film region in these gas-oil interfaces while simultaneously acting as a reinforcing agent in the polymer foam. The resulting foams possessed a porosity of approximately 56%, and the incorporation of cellulose fibres did not affect thermal behaviour. Scanning electron micrographs showed randomly oriented pores with irregular shapes and non-uniform pore size throughout the samples.

SUBMITTER: Obradovic J

PROVIDER: S-EPMC5553527 | biostudies-other | 2017 Jun

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Thermo-Mechanical Behaviour of Flax-Fibre Reinforced Epoxy Laminates for Industrial Applications.

Project description:The present work describes the experimental mechanical characterisation of a natural flax fibre reinforced epoxy polymer composite. A commercial plain woven quasi-unidirectional flax fabric with spun-twisted yarns is employed in particular, as well as unidirectional composite panels manufactured with three techniques: hand-lay-up, vacuum bagging and resin infusion. The stiffness and strength behaviours are investigated under both monotonic and low-cycle fatigue loadings. The analysed material has, in particular, shown a typical bilinear behaviour under pure traction, with a knee yield point occurring at a rather low stress value, after which the material tensile stiffness is significantly reduced. In the present work, such a mechanism is investigated by a phenomenological approach, performing periodical loading/unloading cycles, and repeating tensile tests on previously "yielded" samples to assess the evolution of stiffness behaviour. Infrared thermography is also employed to measure the temperature of specimens during monotonic and cyclic loading. In the first case, the thermal signal is monitored to correlate departures from the thermoelastic behaviour with the onset of energy loss mechanisms. In the case of cyclic loading, the thermoelastic signal and the second harmonic component are both determined in order to investigate the extent of elastic behaviour of the material.

| S-EPMC5458889 | biostudies-other

Characterization of crystalline cellulose of jute reinforced poly (vinyl alcohol) (PVA) biocomposite film for potential biomedical applications.

Project description:Cellulose crystals (CC) were chemically derived from jute by alkali treatment, bleaching and subsequent hydrolysis with 40 % sulfuric acid. Infrared spectroscopy (FT-IR) suggested sufficient removal of lignin and hemicellulose from the raw jute and scanning electron microscopy (SEM), and X-ray diffraction (XRD) studies demonstrated the preparation of microcrystalline cellulose. CC reinforced polyvinyl alcohol (PVA) composite was prepared by solution casting method under laminar flow. In order to maintain uniform dispersion of 3-15 % (w/w) of the CC in the composite N, N dimethylformamide (DMF) was used as a dispersant. FT-IR, XRD, SEM, thermogravimetric analysis (TG, DTG and DTA) and thermomechanical analyses (TMA) were used to characterize the CC and the composites. The study of tensile properties showed that tensile strength (TS) and modulus (TM) increase with increasing CC content up to 9 % and then decrease with the addition of a high content of CC (above 9 %) because of the aggregation of CCs in the composite. The highest TS (43.9 MPa) and TM (2,190 MPa) have been shown to be the composite prepared with 9 % CC and the lowest to be from pure PVA film 17.1 and 1470 MPa. In addition, the composites have showed no cytotoxicity that can also prohibit microbial growth and; hence, it can be a potential material for biomedical applications such as wound healing accelerators.

| S-EPMC5151122 | biostudies-literature

Torsional Behaviour of Steel Fibre Reinforced Alkali Activated Concrete.

Project description:Nine alkali-activated concrete beams were produced and tested under pure torsional load to failure. The alkali-activated concrete beams were produced with following variables: (i) fibres only, (ii) conventionally reinforced or (iii) a hybrid of both fibres and conventional steel reinforcement. The fibres only beams were found to have approximately 20% higher cracking torque than conventionally reinforced beams. However, fibres only beams were observed to have lower post crack ductility and inconsistent post crack behaviour, in comparison to conventionally reinforced alkali-activated concrete (AAC) beams. On the other hand, the hybrid reinforcements in AAC beams were found to demonstrate more ductile post crack behaviour consistently of the beams tested. Hybrid reinforcement was also shown to have 20% and 25% improvement in cracking and ultimate torque compared to conventionally reinforced, which suggests that it is suitable for industrial applications to improve structure capacity. The ultimate torque results of the beams were compared to an analytical model that considered the contribution of fibres. It was found that the ultimate torque of the hybrid reinforced beam has good correlation with the model but overestimated conventionally reinforced beams.

| S-EPMC7435397 | biostudies-literature

Data on acoustic behaviour of coconut fibre-reinforced concrete.

Project description:The data presented in this research show the results of the experimental study of acoustic behaviour of coconut fibre-reinforced concrete (CFRC). The CFRC was added in percentages of 0.25%, 0.5%, 0.75% and 1% of cement. The acoustic test was conducted to determine the amount of sound that can be absorbed by the fibre. The data showed that the concrete reinforced with coconut fibre had the highest sound absorptive power, of which fibre treated absorbed more sound than other fibres, this is because washing of fibre increase the lignin content which is responsible for the sound absorbing property. The data also showed that the curing time had no effect on the absorbing property of the CFRC. The data presented will be useful in the construction of sound proof reinforced concrete slabs, walls and other elements.

| S-EPMC6222070 | biostudies-literature

Woven Natural Fibre Reinforced Composite Materials for Medical Imaging.

Project description:Repeatable patient positioning is key to minimising the burden on planning radiotherapy treatment. There are very few materials commercially available which are suitable for use in all common imaging and treatment modalities such as magnetic resonance imaging (MRI), X-Ray computed tomography (CT) and radiotherapy. In this article, we present several such materials based on woven natural fibres embedded in a range of different resin materials which are suitable for such applications. By investigating a range of resins and natural fibre materials in combination and evaluating their performance in terms of MRI and X-Ray imaging, we show that a woven cotton material impregnated with a two-part epoxy resin provides a 15% improvement in passage of X-Rays and has no impact on the MRI signal (unlike the 40% MRI signal attenuation from carbon fibre), whilst also retaining a flexural modulus up to 71% of that of carbon fibre. These results demonstrate that natural fibre composites produced using such materials provide desirable properties for use in patient support and positioning devices for multi-modal imaging, without the need to significantly compromise on the strength of the material.

| S-EPMC7178646 | biostudies-literature

Preparation of cellulose nanocrystal (CNCs) reinforced polylactic acid (PLA) bionanocomposites filaments using biobased additives for 3D printing applications.

Project description:This work presents the experimental steps taken towards the preparation of 3D printable bionanocomposites using polylactic acid (PLA) biopolymer containing 0.1, 0.5 and 1 wt% CNCs. Optimized amounts of bio-based additives were added to improve the processability and flexibility of the bionanocomposites. The 3D printable bionanocomposite filaments were drawn using a single screw extruder. The bionanocomposites filament was used to 3D print prototypes and test specimens for dynamic mechanical analysis (DMA). Characterization of the CNCs and bionanocomposites was performed using Fourier Transform Infrared Spectroscopy (FTIR) analysis, differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). The nucleating effect of CNCs enhanced the crystallization behaviour of bionanocomposites by 5%, 15% and 11%, for the different CNCs loadings. The TGA analysis revealed a ∼20 °C improvement in the thermal stability of the bionanocomposites. Meanwhile, the tensile analysis showed a ≥48% increase in the tensile strength of the bionanocomposites filaments which was attributed to the reinforcing effects of CNC. The addition of CNCs significantly increased the melt viscosity, storage and loss modulus of PLA. In summary, the bionanocomposite filaments produced in this study exhibited excellent processibility and superior mechanical and thermal properties.

| S-EPMC10448353 | biostudies-literature

Cellulose Fibre Degradation in Cellulose/Steel Hybrid Geotextiles under Outdoor Weathering Conditions.

Project description:Risks from rockfall and land sliding can be controlled by high-tensile steel nets and meshes which stabilise critical areas. In many cases, a recultivation of the land is also desired. However, high-tensile steel meshes alone are not always sufficient, depending on the location and the inclination of the stabilised slope, to achieve rapid greening. Cellulose fibres exhibit high water binding capacity which supports plant growth. In this work, a hybrid structure consisting of a nonwoven cellulose fibre web and a steel mesh was produced and tested under outdoor conditions over a period of 61 weeks. The cellulose fibres are intended to support plant growth and soil fixation, and thus the biodegradation of the structure is highly relevant, as these fibres will become part of the soil and must be biodegradable. The biodegradation of the cellulose fibres over the period of outdoor testing was monitored by microscopy and analytical methods. The enzymatic degradation of the cellulose fibres led to a reduction in the average degree of polymerisation and also a reduction in the moisture content, as polymer chain hydrolysis occurs more rapidly in the amorphous regions of the fibres. FTIR analysis and determination of carboxylic group content did not indicate substantial changes in the remaining parts of the cellulose fibre. Plant growth covered geotextiles almost completely during the period of testing, which demonstrated their good compatibility with the greening process. Over the total period of 61 weeks, the residual parts of the biodegradable cellulose web merged with the soil beneath and growing plants. This indicates the potential of such hybrid concepts to contribute a positive effect in greening barren and stony land, in addition to the stabilising function of the steel net.

| S-EPMC9573017 | biostudies-literature

A cellulose nanofibril-reinforced hydrogel with robust mechanical, self-healing, pH-responsive and antibacterial characteristics for wound dressing applications.

Project description:BackgroundBacterial infection in wounds has become a major threat to human life and health. With the growth use of synthetic antibiotics and the elevated evolution of drug resistant bacteria in human body cells requires the development of novel wound curing strategies. Herein, a novel pH-responsive hydrogel (RPC/PB) was fabricated using poly(vinyl alcohol)-borax (PB) and natural antibiotic resveratrol grafted cellulose nanofibrils (RPC) for bacterial-infected wound management.ResultsIn this hydrogel matrix, RPC conjugate was interpenetrated in the PB network to form a semi-interpenetrating network that exhibited robust mechanical properties (fracture strength of 149.6 kPa), high self-healing efficiency (> 90%), and excellent adhesion performance (tissue shear stress of 54.2 kPa). Interestingly, the induced RPC/PB hydrogel showed pH-responsive drug release behavior, the cumulative release amount of resveratrol in pH 5.4 was 2.33 times than that of pH 7.4, which was adapted well to the acidic wound microenvironment. Additionally, this RPC/PB hydrogel exhibited excellent biocompatibility and antioxidant effect. Moreover, in vitro and in vivo results revealed that such RPC/PB hydrogel had excellent antibacterial, skin tissue regeneration and wound closure capabilities.ConclusionTherefore, the generated RPC/PB hydrogel could be an excellent wound dressing for bacteria-infected wound healing.

| S-EPMC9258071 | biostudies-literature

Nanofibrillated Bacterial Cellulose Modified with (3-Aminopropyl)trimethoxysilane under Aqueous Conditions: Applications to Poly(methyl methacrylate) Fiber-Reinforced Nanocomposites.

Project description:The development of eco-friendly fiber-reinforced composite resins is an important objective from an environmental perspective, and nanofibrillated bacterial cellulose (NFBC), with extremely long high-aspect-ratio fibers, is a filler material with high potential for use in such composite resins. In this study, we investigated chemical modification of the surfaces of NFBC fibers by coupling with (3-aminopropyl)trimethoxysilane and fabricated nanocomposite materials using the prepared surface-modified NFBC. The product prepared by the one-pot reaction of (3-aminopropyl)trimethoxysilane with NFBC microfibrils dispersed in aqueous acid retained the same nanofibril structure as the intact NFBC. The degree of molar substitution and the silicon states on the surface of the product depended on the NFBC/(3-aminopropyl)trimethoxysilane ratio. The thermal analysis revealed that the thermal degradation temperature of the products increases with an increase of degree of molar substitution. Highly transparent (78-89% at 600 nm) poly(methyl methacrylate)-based nanocomposites were prepared by solvent casting; the nanocomposite containing 1.0 wt % (3-aminopropyl)trimethoxysilylated NFBC was only 8% less transparent than neat poly(methyl methacrylate) at 600 nm. In addition, the tensile strength of the nanocomposite was more than twice that of neat poly(methyl methacrylate) when 1 wt % of the surface-modified NFBC was added. The surface-modified NFBC is expected to be a reinforcing nanofiber material that imparts excellent physical properties to fiber-reinforced resins.

| S-EPMC7676300 | biostudies-literature

Nanoscopic origin of cracks in carbon fibre-reinforced plastic composites.

Project description:Voids and cracks can fatally degrade structural materials such as metals and ceramics but are tolerated in carbon fibre-reinforced plastic (CFRP) composites if monitored to prevent their growth to a critical size. Thus, the use of CFRPs as aeronautical structural materials requires an understanding of microscopic crack formation. However, this crack-formation mechanism remains unclear because experimental difficulties have hindered studies of relevant phenomena that occur before crack formation. Herein, we report high-resolution (~50?nm) and non-destructive three-dimensional observations of crack initiation and propagation under applied stress. This evaluation reveals that voids and cracks do not simply result from local stresses but instead occur largely through two competing nanoscale mechanisms, namely, fibre/plastic interface debonding and in-plastic crack initiation. Therefore, nanoscopic insights into these heterogeneities are essential for controlling crack initiation and determining reasonable safety margins for CFRP composite use.

| S-EPMC6917772 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data