Hydrolysis of Cellulose by a Mesoporous Carbon-Fe?(SO?)?/?-Fe?O? Nanoparticle-Based Solid Acid Catalyst.

ABSTRACT: Carbon-based solid acid catalysts have shown significant potential in a wide range of applications, and they have been successfully synthesized using simple processes. Magnetically separable mesoporous carbon composites also have enormous potential, especially in separation and adsorption technology. However, existing techniques have been unable to produce a magnetically separable mesoporous solid acid catalyst because no suitable precursors have been identified. Herein we describe a magnetically separable, mesoporous solid acid catalyst synthesized from a newly developed mesoporous carbon-?-Fe2O3 nanoparticle composite. This material exhibits an equivalent acid density and catalytic activity in the hydrolysis of microcrystalline cellulose, to that of the cellulose-derived conventional catalyst. Since it is magnetically separable, this material can be readily recovered and reused, potentially reducing the environmental impact of industrial processes to which it is applied.

SUBMITTER: Yamaguchi D

PROVIDER: S-EPMC4746576 | biostudies-literature | 2016 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Carbon Nanoparticle-Loaded Iron [CNSI-Fe(II)] in the Treatment of Advanced Solid Tumor

Project description:This Phase I clinical trial aims to evaluate the safety, tolerability, pharmacokinetics (PK) profile and preliminary efficacy of intratumoral injection of Carbon Nanoparticle-Loaded Iron [CNSI-Fe(II)] in patients with advanced solid tumors. The study also aims to observe dose-limiting toxicities (DLT) of CNSI-Fe(II) to determine the maximum tolerated dose (MTD) or the highest injectable dose in humans, providing dosing guidelines for future clinical studies. CNSI-Fe(II) shows promise as an innovative tumor therapeutic agent due to its unique properties of ferroptosis. The study primarily focuses on assessing the potential efficacy of CNSI-Fe(II) in patients with advanced solid tumors, particularly in patients with Kras mutation, e.g., pancreatic cancer patients.

| 92811 | ecrin-mdr-crc

Nano-sized mesoporous phosphated tin oxide as an efficient solid acid catalyst.

Project description:Herein, we prepared a mesoporous tin oxide catalyst (mSnO2) activated with phosphate species by the adsorption of phosphate ions from a phosphoric acid solution onto tin oxyhydroxide (Sn(OH)4) surface. The phosphate content ranged from 3 to 45 wt%. The nonaqueous titration of n-butylamine in acetonitrile was used to determine the total surface acidity level. FTIR of chemically adsorbed pyridine was used to differentiate between the Lewis and Brönsted acid sites. Thermal and X-ray diffraction analysis indicated that the addition of phosphate groups stabilized the mesostructure of mSnO2 and enabled it to keep its crystalline size at the nanoscale. FTIR analysis indicated the polymerization of the HPO4 2- groups into P2O7 4-, which in turn reacts with SnO2 to form a SnP2O7 layer, which stabilizes the mesoporous structure of SnO2. The acidity measurements showed that the phosphate species are distributed homogeneously over the mSnO2 surface until surface saturation coverage at 25 wt% PO4 3-, at which point the acid strength and surface acidity level are maximized. The catalytic activity was tested for the synthesis of hydroquinone diacetate, where it was found that the % yield of hydroquinone diacetate compound increased gradually with the increase in PO4 3- loading on mSnO2 until it reached a maximum value of 93.2% for the 25% PO4 3-/mSnO2 catalyst with 100% selectivity and excellent reusability for three consecutive runs with no loss in activity.

| S-EPMC9059524 | biostudies-literature

Simultaneous Fe<sub>3</sub>O<sub>4</sub> Nanoparticle Formation and Catalyst-Driven Hydrothermal Cellulose Degradation.

Project description:Breakdown and utilization of cellulose are critical for the bioenergy sector; however, current cellulose-to-energy conversion schemes often consume large quantities of unrecoverable chemicals, or are expensive, due to the need for enzymes or high temperatures. In this paper, we demonstrate a new method for converting cellulose into soluble compounds using a mixture of Fe2+ and Fe3+ as catalytic centers for the breakdown, yielding Fe3O4 nanoparticles during the hydrothermal process. Iron precursors transformed more than 61% of microcrystalline cellulose into solutes, with the composition of the solute changing with the initial Fe3+ concentration. The primary products of the breakdown of cellulose were a range of aldaric acids with different molecular weights. The nanoparticles have concentration-dependent tuneable sizes between 6.7 and 15.8 nm in diameter. The production of value-added nanomaterials at low temperatures improves upon the economics of traditional cellulose-to-energy conversion schemes with the precursor value increasing rather than deteriorating over time.

| S-EPMC8153760 | biostudies-literature

Effect of Acid Hydrolysis Conditions on the Properties of Cellulose Nanoparticle-Reinforced Polymethylmethacrylate Composites.

Project description:Cellulose nanoparticles (CNPs) were prepared from microcrystalline cellulose using two concentration levels of sulfuric acid (i.e., 48 wt% and 64 wt% with produced CNPs designated as CNPs-48 and CNPs-64, respectively) followed by high-pressure homogenization. CNP-reinforced polymethylmethacrylate (PMMA) composite films at various CNP loadings were made using solvent exchange and solution casting methods. The ultraviolet-visible (UV-vis) transmittance spectra between 400 and 800 nm showed that CNPs-64/PMMA composites had a significantly higher optical transmittance than that of CNPs-48/PMMA. Their transmittance decreased with increased CNP loadings. The addition of CNPs to the PMMA matrix reduced composite's coefficient of thermal expansion (CTE), and CNPs-64/PMMA had a lower CTE than CNPs-48/PMMA at the same CNP level. Reinforcement effect was achieved with the addition of CNPs to the PMMA matrix, especially at higher temperature levels. CNPs-64/PMMA exhibited a higher storage modulus compared with CNPs-48/PMMA material. All CNP-reinforced composites showed higher Young's modulus and tensile strengths than pure PMMA. The effect increased with increased CNP loadings in the PMMA matrix for both CNPs-64/PMMA and CNPs-48/PMMA composites. CNPs affected the Young's modulus more than they affected the tensile strength.

| S-EPMC5453138 | biostudies-other

Selective Synthesis of Oligosaccharides by Mechanochemical Hydrolysis of Chitin over a Carbon-Based Catalyst.

Project description:Oligosaccharides possess fascinating functions that are applicable in a variety of fields, such as agriculture. However, the selective synthesis of oligosaccharides, especially chitin-oligosaccharides, has remained a challenge. Chitin-oligosaccharides activate the plant immune system, enabling crops to withstand pathogens without harmful agrichemicals. Here, we demonstrate the conversion of chitin to chitin-oligosaccharides using a carbon catalyst with weak acid sites and mechanical milling. The catalyst produces chitin-oligosaccharides with up to 94 % selectivity in good yields. Monte-Carlo simulations indicate that our system preferentially hydrolyzes larger chitin molecules over oligomers, thus providing the desired high selectivity. This unique kinetics is in contrast to the fact that typical catalytic systems rapidly hydrolyze oligomers to monomers. Unlike other materials carbons more strongly adsorb large polysaccharides than small oligomers, which is suitable for the selective synthesis of small oligosaccharides.

| S-EPMC10099807 | biostudies-literature

Fabrication of a Novel and High-Performance Mesoporous Ethylene Tar-Based Solid Acid Catalyst for the Dehydration of Fructose into 5-Hydroxymethylfurfural.

Project description:In this article, a novel and high-performance mesoporous carbon-based solid acid catalyst was prepared using ethylene tar (ET) as a precursor, which is a byproduct of ethylene production. First, ET was carbonized at 550 °C by using magnesium acetate as the template. After that, the mesoporous ET-based solid acid catalyst was obtained by a one-step sulfonation process that removes the templates simultaneously. On the basis of these facts, the maximum yield of 5-hydroxymethylfurfural (5-HMF) in the presence of an ET catalyst during the dehydration of fructose can reach 87.8%. This effective catalytic activity is mainly attributed to the large specific surface area and high density of sulfonic acid groups existing in the ET catalyst. Moreover, no distinct activity drop was observed during five recycling runs that confirmed good recyclability and thermal stability of the ET catalyst. This research provides a novel and promising method for the utilization of ET as a low-cost, recyclable, and high-performance catalyst.

| S-EPMC6644591 | biostudies-literature

Ring-opening hydrolysis of spiro-epoxyoxindoles using a reusable sulfonic acid functionalized nitrogen rich carbon catalyst.

Project description:Controlling the product selectivity of a ring-opening hydrolysis reaction remains a great challenge with mineral acids and to an extent with homogeneous catalysts. In addition, even trace amounts of metal impurities in a bioactive product hinder the reaction progress. This has necessitated the development of robust and metal-free catalysts to offer an alternative sustainable route. We report a nitrogen-rich sulfonated carbon as a catalyst derived from an inexpensive precursor for the synthesis of bioactive vicinal diols of spiro-oxindole derivatives. The well-characterized catalyst shows wide generality with different electronic and steric substituents in the substrates under mild reaction conditions. Hot filtration test confirms no leaching of the acid moiety and the catalyst could be reused for four cycles with retention of activities.

| S-EPMC8697273 | biostudies-literature

Visualizing Degradation of Cellulose Nanofibers by Acid Hydrolysis.

Project description:Cellulose hydrolysis is an extensively studied process due to its relevance in the fields of biofuels, chemicals production, and renewable nanomaterials. However, the direct visualization of the process accompanied with detailed scaling has not been reported because of the vast morphological alterations occurring in cellulosic fibers in typical heterogeneous (solid/liquid) hydrolytic systems. Here, we overcome this distraction by exposing hardwood cellulose nanofibers (CNFs) deposited on silica substrates to pressurized HCl gas in a solid/gas system and examine the changes in individual CNFs by atomic force microscopy (AFM). The results revealed that hydrolysis proceeds via an intermediate semi-fibrous stage before objects reminiscent of cellulose nanocrystals were formed. The length of the nanocrystal-like objects correlated well with molar mass, as analyzed by gel permeation chromatography, performed on CNF aerogels hydrolyzed under identical conditions. Meanwhile, X-ray diffraction showed a slight increase in crystallinity index as the hydrolysis proceeded. The results provide a modern visual complement to >100 years of research in cellulose degradation.

| S-EPMC8045026 | biostudies-literature

Catalyst-free synthesis of transparent, mesoporous diamond monoliths from periodic mesoporous carbon CMK-8.

Project description:We report on the synthesis of optically transparent, mesoporous, monolithic diamond from periodic mesoporous carbon CMK-8 at a pressure of 21 GPa. The phase transformation is already complete at a mild synthesis temperature of 1,300 degrees C without the need of a catalyst. Surprisingly, the diamond is obtained as a mesoporous material despite the extreme pressure. X-ray diffraction, SEM, transmission electron microscopy, selected area electron diffraction, high-resolution transmission electron microscopy, and Z-contrast experiments suggest that the mesoporous diamond is composed of interconnected diamond nanocrystals having diameters around 5-10 nm. The Brunauer Emmett Teller surface area was determined to be 33 m2 g(-1) according Kr sorption data. The mesostructure is diminished yet still detectable when the diamond is produced from CMK-8 at 1,600 degrees C and 21 GPa. The temperature dependence of the porosity indicates that the mesoporous diamond exists metastable and withstands transformation into a dense form at a significant rate due to its high kinetic inertness at the mild synthesis temperature. The findings point toward ultrahard porous materials with potential as mechanically highly stable membranes.

| S-EPMC2922285 | biostudies-literature

Statistical Optimization for Acid Hydrolysis of Microcrystalline Cellulose and Its Physiochemical Characterization by Using Metal Ion Catalyst.

Project description:Hydrolyzing the amorphous region while keeping the crystalline region unaltered is the key technology for producing nanocellulose. This study investigated if the dissolution properties of the amorphous region of microcrystalline cellulose can be enhanced in the presence of Fe3+ salt in acidic medium. The process parameters, including temperature, time and the concentration of metal chloride catalyst (FeCl₃), were optimized by using the response surface methodology (RSM). The experimental observation demonstrated that temperature and time play vital roles in hydrolyzing the amorphous sections of cellulose. This would yield hydrocellulose with higher crystallinity. The factors that were varied for the production of hydrocellulose were the temperature (x₁), time (x₂) and FeCl₃ catalyst concentration (x₃). Responses were measured in terms of percentage of crystallinity (y₁) and the yield (y₂) of the prepared hydrocellulose. Relevant mathematical models were developed. Analysis of variance (ANOVA) was carried out to obtain the most significant factors influencing the responses of the percentage of crystallinity and yield. Under optimum conditions, the percentage of crystallinity and yield were 83.46% and 86.98% respectively, at 90.95 °C, 6 h, with a catalyst concentration of 1 M. The physiochemical characteristics of the prepared hydrocellulose were determined in terms of XRD, SEM, TGA and FTIR analyses. The addition of FeCl₃ salt in acid hydrolyzing medium is a novel technique for substantially increasing crystallinity with a significant morphological change.

| S-EPMC5456008 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data