Anti-Bacteria and Microecosystem-Regulating Effects of Dental Implant Coated with Dimethylaminododecyl Methacrylate.

ABSTRACT: The effects of dimethylaminododecyl methacrylate (DMADDM) modified titanium implants on bacterial activity and microbial ecosystem of saliva-derived biofilm were investigated for the first time. Titanium discs were coated with DMADDM solutions at mass fractions of 0 mg/mL (control), 1, 5 and 10 mg/mL, respectively. Biomass accumulation and metabolic activity of biofilms were tested using crystal violet assay and MTT (3-(4,5-Dimethyl-thiazol-2-yl)-2,5-diphenyltetrazolium bromide) assay. 16S rRNA gene sequencing was performed to measure the microbial community. Live/dead staining and scanning electron microscopy (SEM) were used to value the structure of biofilm. The results showed that the higher mass fraction of DMADDM the coating solution had, the significantly lower the values of metabolic activity and accumulated biofilms got, as well as fewer live cells and less extracellular matrix. Moreover, 5 mg/mL of DMADDM was the most effective concentration, as well as 10 mg/mL. In microecosystem-regulation, the DMADDM modified titanium implant decreased the relative abundance of Neisseria and Actinomyces and increased the relative abundance of Lactobacillus, a probiotic for peri-implant diseases. In conclusion, via inhibiting growth and regulating microecosystem of biofilm, this novel titanium implant coating with DMADDM was promising in preventing peri-implant disease in an 'ecological manner'.

SUBMITTER: Li B

PROVIDER: S-EPMC6150392 | biostudies-literature | 2017 Nov

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Anti-Bacteria and Microecosystem-Regulating Effects of Dental Implant Coated with Dimethylaminododecyl Methacrylate.

Li Bolei B Ge Yang Y Wu Yao Y Chen Jing J Xu Hockin H K HHK Yang Minggang M Li Mingyun M Ren Biao B Feng Mingye M Weir Michael D MD Peng Xian X Cheng Lei L Zhou Xuedong X

Molecules (Basel, Switzerland) 20171120 11

The effects of dimethylaminododecyl methacrylate (DMADDM) modified titanium implants on bacterial activity and microbial ecosystem of saliva-derived biofilm were investigated for the first time. Titanium discs were coated with DMADDM solutions at mass fractions of 0 mg/mL (control), 1, 5 and 10 mg/mL, respectively. Biomass accumulation and metabolic activity of biofilms were tested using crystal violet assay and MTT (3-(4,5-Dimethyl-thiazol-2-yl)-2,5-diphenyltetrazolium bromide) assay. 16S rRNA ...[more]

PMID: 29156630

Similar Datasets

Project description:ObjectivesThe susceptibility of methacrylates to hydrolytic and enzymatic degradation may be a contributing factor limiting the clinical lifespan of resin composite restorations. The elimination of labile ester bonds is a potential advantage of methacrylamides, which have been shown to produce more stable restorative interfaces. The rationale of this study is to design hydrolytically and enzymatically stable adhesive monomers, with the added benefit of being able to form crosslinked networks. The objective of this study was to synthesize difunctional, hybrid methacrylate-methacrylamide monomers, and evaluate them as potential monomers for dental adhesives.Materials and methodsHEMA, TEGDMA (controls) or secondary methacrylamides (HEMAM - commercially available, 2EM and 2dMM - newly synthesized) either bearing a hydroxyl group or a methacrylate functionality (Hybrids-Hy), were added at 40mass% to bisGMA. The photoinitiator system consisted of 2-dimethoxyphenyl acetophenone (DMPA) and diphenyl iodonium hexafluorophosphate (DPI-PF6) at 0.2 and 0.4mass%, respectively. Polymerization kinetics were followed in real-time by near-IR spectroscopy during light activation at 630mW/cm2 for 300s. Water sorption and solubility (WS, SL) were measured according to ISO 4049. Storage modulus in shear (G') for 300s was obtained by oscillatory rheometry. For the microtensile bond strength (μTBS), fully formulated adhesives containing 40vol% ethanol were used to restore caries-free human third molars. Bonded specimens with 1mm2 cross-sectional area were tested after 48h and 6 months storage in water at 37°C. Single bond (SB) was tested as a commercial control. Data were analysed with one-way ANOVA and Tukey's test and Student's t-test (α=0.05).ResultsIn general, hybrid versions showed lower polymerization rate and degree of conversion, whereas the methacrylate controls, HEMA and TEGDMA, showed the highest values. The hybrid versions showed lower values of WS and SL than their monofunctional versions. HEMAM Hy showed the highest values of G' and TEGDMA, 2EM, and 2dMM-Hy the lowest. The μTBS values between 48h and 6 months were statistically reduced only for the HEMA and both 2dMM materials. The formulation containing the monofunctional methacrylamide (HEMAM) showed only 9% reduction in μTBS after 6 months of aging, while the other groups showed a decrease ranging between 18% and 33%.ConclusionOverall, hybrid monomers showed lower reactivity than their analogous monofunctional versions, but had markedly lower water sorption. Shear storage modulus was affected differently by the addition of the second functionality. HEMAM-containing systems were able to maintain stable long-term dentin bond strength, which demonstrates that bonding stability is a result of the complex interplay among the factors studied.Clinical significanceThe novel monomers showed here are potential alternatives to the current methacrylate adhesives, with selected formulations presenting greater bond stability.

Project description:Investigation of polymerisation kinetics using ATR-FTIR systems is common in many dental studies. However, peak selection methods to calculate monomer-polymer conversion can vary, consequently affecting final results. Thus, the aim of this study is to experimentally confirm which method is less prone to systematic errors. Three commercial restorative materials were tested-Vertise Flow (VF), Constic and Activa Bioactive Restorative Kids. Firstly, Attenuated Total Reflectance Fourier Transform Infra-Red (ATR-FTIR) (Spectrum One, Perkin-Elmer, UK) spectra of monomers were acquired-10-methacryloyloxy decyl dihydrogen phosphate (10-MDP), bisphenol-A glycidyl dimethacrylate (Bis-GMA), 2-hydroxyethyl methacrylate (HEMA), triethyelene glycol dimethacrylate (TEGDMA) and urethane dimethacrylate (UDMA) to investigate proportionality of methacrylate peak heights versus concentration. Spectral changes upon light exposure of 2 mm discs of the restorative materials (irradiated for 20 s, LED curing unit 1100-1330 mW/cm2) were assessed to study polymerisation kinetics (n = 3), with continuous acquisition of spectra, before, during and after light exposure. Peak differences and degrees of conversion (DC %) were calculated using 1320/1336, 1320/1350 and 1636/1648 cm-1 as reaction/reference peaks. Inferential statistics included a MANOVA and within-subjects repeated measures ANOVA design (5% significance level). Proportionality of methacrylate peak height to concentration was confirmed, with the 1320/1352 cm-1 peak combination showing the lowest coefficient of variation (8%). Difference spectra of the polymerisation reaction showed noise interference around the 1500-1800 cm-1 region. Across the different materials, DC % results are highly dependent upon peak selection (p<0.001), with higher variability associated to the 1636 cm-1. Significant differences in the materials were only detected when the 1320 cm-1 peak was used (p<0.05). Within the same materials, methods were significantly different for Constic and Activa (p<0.05). It is possible to conclude that the 1320 cm-1 peak is more adequate to assess polymerisation of methacrylates and is therefore recommended.

Dataset Information

Anti-Bacteria and Microecosystem-Regulating Effects of Dental Implant Coated with Dimethylaminododecyl Methacrylate.

Publications

Anti-Bacteria and Microecosystem-Regulating Effects of Dental Implant Coated with Dimethylaminododecyl Methacrylate.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure