A Biorefinery Strategy That Introduces Hydrothermal Treatment Prior to Acid Hydrolysis for Co-generation of Furfural and Cellulose Nanocrystals.

ABSTRACT: Hydrothermal treatment of wood pulp at 150–225°C prior to acid hydrolysis was investigated in the context of isolating cellulose nanocrystals (CNCs). The objective was 2-folds as follows: (a) generating furfural as a value–added co–product; and (b) concentrating and forming new CNC precursors through thermal re–orientation of para–crystalline cellulose chains that will in turn improve CNC recovery and yield. Furfural yields up to 19 and 21% xylan conversion were obtained at 200 and 225°C hydrothermal treatments, respectively. In addition, these hydrothermal treatment conditions increased the crystallinity index of the pulp (77%) to 84 and 80%, respectively. Consequently, the CNC yield from hydrothermally treated wood pulp, when compared to untreated wood pulp, improved by up to 4- and 2-folds, respectively. An efficient acid hydrolysis process with yield improvements can translate to reduced CNC isolation and purification costs and increased production capacity. The qualities of the CNCs in terms of particle size and crystallinity were not affected due to hydrothermal treatment. However, the zeta potential, sulfur, hydrogen, and oxygen content of the CNCs were significantly lower at 225°C while carbon composition increased, and dark brown coloration was observed that indicates caramelization. This study demonstrates for the first time a novel biorefinery strategy that introduces hydrothermal treatment prior to acid hydrolysis to co–generate furfural and CNC with improved efficiency.

SUBMITTER: Beyene D

PROVIDER: S-EPMC7189013 | biostudies-literature | 2020

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Structural Effects of Cellulose on Hydrolysis and Carbonization Behavior during Hydrothermal Treatment.

Project description:This study aims to investigate how the morphology of cellulose influences the hydrolysis and carbonization during hydrothermal treatment at temperatures between 180 and 240 °C. The morphology of cellulose, especially different crystallinities and degrees of polymerization, is represented by microcrystalline cellulose and α-cellulose. Kinetic analysis is considered a tool to allow the determination of the mechanisms of the two types of cellulose during the hydrothermal process. A kinetic model, in which cellulose is assumed to be hydrolyzed to a limited extent, is proposed. Five scenarios are used as models for pyrolysis of nonhydrolyzed cellulose that forms primary char, along with reaction pathways of hydrolyzable cellulose and its derivatives that latterly form secondary char. The morphologies of solid products are in good agreement with the results of the proposed model.

| S-EPMC7271358 | biostudies-literature

Preparation of Spherical Cellulose Nanocrystals from Microcrystalline Cellulose by Mixed Acid Hydrolysis with Different Pretreatment Routes.

Project description:Spherical cellulose nanocrystal (CNC), as a high value cellulose derivative, shows an excellent application potential in biomedicine, food packaging, energy storage, and many other fields due to its special structure. CNC is usually prepared by the mixed acid hydrolysis method from numerous cellulose raw materials. However, the pretreatment route in preparing spherical CNC from cellulose fiber is still used when choosing microcrystalline cellulose (MCC) as the raw material, which is not rigorous and economical. In this work, pretreatment effects on the properties of spherical CNC produced from MCC by mixed acid hydrolysis were systematically studied. Firstly, the necessity of the swelling process in pretreatment was examined. Secondly, the form effects of pretreated MCC (slurry or powder form) before acid hydrolysis in the preparation of spherical CNC were carefully investigated. The results show that the swelling process is not indispensable. Furthermore, the form of pretreated MCC also has a certain influence on the morphology, crystallinity, and thermal stability of spherical CNC. Thus, spherical CNC with different properties can be economically prepared from MCC by selecting different pretreatment routes through mixed acid hydrolysis.

| S-EPMC9502823 | biostudies-literature

Alkali Hydrolysis of Sulfated Cellulose Nanocrystals: Optimization of Reaction Conditions and Tailored Surface Charge.

Project description:Cellulose nanocrystals (CNCs) are a biorenewable resource, which may be chemically modified to impart specific properties. Modified CNCs have found use in imaging applications, as rheology modifiers, polymer reinforcements, barrier and/or optical films, and nanocomposites. Nanoparticle dimensions of CNCs are typically 5-10 nm in width, with lengths of <100-300 nm. However, the physical properties are dependent upon the number and nature of the surface charge groups imparted during preparation. In the case of CNCs produced from sulfuric acid hydrolysis, the sulfated surface groups may be partially removed prior to further functionalization. This gives more available hydroxyls yet renders the CNCs less colloidally stable. Furthermore, conditions vary significantly and there is no consensus about the optimal conditions for partial removal of sulfate functionality or conditions developed to give specific surface charge. In the following, alkali hydrolysis of sulfate half-esters was quantified by conductometric titration of the strong acid groups, and using a design of experiments (DOE), optimal conditions were determined to produce CNCs with tailored surface charge.

| S-EPMC6780348 | biostudies-literature

Enzymatic Hydrolysis of Bacterial Cellulose for the Production of Nanocrystals for the Food Packaging Industry.

Project description:Bacterial cellulose nanocrystals (BCNCs) obtained by enzymatic hydrolysis have been loaded in pullulan biopolymer for use as nanoparticles in the generation of high-oxygen barrier coatings intended for food packaging applications. Bacterial cellulose (BC) produced by Komagataeibacter sucrofermentans was hydrolyzed by two different enzymatic treatments, i.e., using endo-1,4-?-glucanases (EGs) from Thermobifida halotolerans and cellulase from Trichoderma reesei. The hydrolytic activity was compared by means of turbidity experiments over a period of 145 h, whereas BCNCs in their final state were compared, in terms of size and morphology, by atomic force microscopy (AFM) and dynamic light scattering (DLS). Though both treatments led to particles of similar size, a greater amount of nano-sized particles (?250 nm) were observed in the system that also included cellulase enzymes. Unexpectedly, transmission electron microscopy (TEM) revealed that cellulose nanoparticles were round-shaped and made of 4-5 short (150-180 nm) piled whiskers. Pullulan/BCNCs nanocomposite coatings allowed an increase in the overall oxygen barrier performance, of more than two and one orders of magnitude (?0.7 mL·m-2·24 h-1), of pure polyethylene terephthalate (PET) (?120 mL·m-2·24 h-1) as well as pullulan/coated PET (?6 mL·m-2·24 h-1), with no significant difference between treatments (hydrolysis mediated by EGs or with the addition of cellulase). BCNCs obtained by enzymatic hydrolysis have the potential to generate high oxygen barrier coatings for the food packaging industry.

| S-EPMC7221805 | biostudies-literature

Total utilization of lignin and carbohydrates in <i>Eucalyptus grandis</i>: an integrated biorefinery strategy towards phenolics, levulinic acid, and furfural.

Project description:BackgroundLignocellulosic biomass, which is composed of cellulose, hemicellulose and lignin, represents the most abundant renewable carbon source with significant potential for the production of sustainable chemicals and fuels. Current biorefineries focus on cellulose and hemicellulose valorization, whereas lignin is treated as a waste product and is burned to supply energy to the biorefineries. The depolymerization of lignin into well-defined mono-aromatic chemicals suitable for downstream processing is recognized increasingly as an important starting point for lignin valorization. In this study, conversion of all three components of Eucalyptus grandis into the corresponding monomeric chemicals was investigated using solid and acidic catalyst in sequence.ResultsLignin was depolymerized into well-defined monomeric phenols in the first step using a Pd/C catalyst. The maximum phenolic monomers yield of 49.8 wt% was achieved at 240 °C for 4 h under 30 atm H2. In the monomers, 4-propanol guaiacol (12.9 wt%) and 4-propanol syringol (31.9 wt%) were identified as the two major phenolic products with 90% selectivity. High retention of cellulose and hemicellulose pulp was also obtained, which was treated with FeCl3 catalyst to attain 5-hydroxymethylfurfural, levulinic acid and furfural simultaneously. The optimal reaction condition for the co-conversion of hemicellulose and cellulose was established as 190 °C and 100 min, from which furfural and levulinic acid were obtained in 55.9% and 73.6% yields, respectively. Ultimately, 54% of Eucalyptus sawdust can be converted into well-defined chemicals under such an integrated biorefinery method.ConclusionsA two-step process (reductive catalytic fractionation followed by FeCl3 catalysis) allows the fractionation of all the three biopolymers (cellulose, hemicellulose, and lignin) in Eucalyptus biomass, which provides a promising strategy to make high-value chemicals from sustainable biomass.

| S-EPMC6943948 | biostudies-literature

An anion-induced hydrothermal oriented-explosive strategy for the synthesis of porous upconversion nanocrystals.

Project description:Rare-earth (RE)-doped upconversion nanocrystals (UCNCs) are deemed as the promising candidates of luminescent nanoprobe for biological imaging and labeling. A number of methods have been used for the fabrication of UCNCs, but their assembly into porous architectures with desired size, shape and crystallographic phase remains a long-term challenging task. Here we report a facile, anion-induced hydrothermal oriented-explosive method to simultaneously control size, shape and phase of porous UCNCs. Our results confirmed the anion-induced hydrothermal oriented-explosion porous structure, size and phase transition for the cubic/hexagonal phase of NaLuF4 and NaGdF4 nanocrystals with various sizes and shapes. This general method is very important not only for successfully preparing lanthanide doped porous UCNCs, but also for clarifying the formation process of porous UCNCs in the hydrothermal system. The synthesized UCNCs were used for in vitro and in vivo CT imaging, and could be acted as the potential CT contrast agents.

| S-EPMC4350008 | biostudies-literature

Isolation of Cellulose Nanocrystals from Banana Peel Using One-Pot Microwave and Mild Oxidative Hydrolysis System.

Project description:The current investigation deals with the application of a one-pot system to facilitate the production of cellulose nanocrystals (CNCs) from banana peel by a combination of microwave pre-treatment and mild oxidative hydrolysis with hydrogen peroxide (H2O2, 0-30 wt%) and sulfuric acid (H2SO4, 0-10%). H2O2 causes decolorization of the banana peel suspension from dark brown to light yellow, while further treatment with H2SO4 produces a white suspension, indicating successful removal of the non-cellulosic components from the banana peel. This finding was further supported by Fourier Transform Infrared (FTIR) spectroscopic analysis, which showed the gradual disappearance of lignin and hemicellulose peaks with increasing H2O2 and H2SO4 concentrations. The CNCs has considerably high crystallinity, with the highest crystallinity (~85%) being obtained at 6% H2SO4. Therefore, CNCs obtained at 6% H2SO4 were selected for further characterization. Scanning Electron Microscope (SEM) analysis confirmed the disintegration of the cellulose fibres into small fragments after hydrolysis. Transmission Electron Microscope (TEM) and Atomic Force Microscope (AFM) analyses revealed the spherical shape of the CNCs with an average size of approximately 20 nm. The CNCs have good stability with zeta potential of -42.9 mV. Findings from this study suggest that the combination of microwave pre-treatment and oxidative hydrolysis with 30 wt% H2O2 and 6% H2SO4, which is about 11 times lower than the commonly used H2SO4 concentration, is proven effective for the isolation of CNCs from banana peel. These observations are expected to provide insight into a facile and environmentally benign alternative to the conventional CNCs isolation method, using abundant and underutilized agricultural waste as feedstock.

| S-EPMC9565709 | biostudies-literature

Optimization of the Obtaining of Cellulose Nanocrystals from Agave tequilana Weber Var. Azul Bagasse by Acid Hydrolysis.

Project description:A multilevel factorial design of 23 with 12 experiments was developed for the preparation of cellulose nanocrystals (CNC) from Agave tequilana Weber var. Azul bagasse, an agro-industrial waste from tequila production. The studied parameters were acid type (H2SO4 and HCl), acid concentration (60 and 65 wt% for H2SO4, 2 and 8N for HCl) temperature (40 and 60 °C for H2SO4, 50 and 90 °C for HCl), and hydrolysis time (40, 55 and 70 min for H2SO4; and 30, 115 and 200 min for HCl). The obtained CNC were physical and chemically characterized using dynamic light scattering (DLS), atomic force microscopy (AFM), Fourier-transform infrared spectroscopy (FT-IR), X-ray photoelectron spectroscopy (XPS), and X-ray diffraction (XDR) techniques. The maximum CNC yield was 90 and 96% for HCL and H2SO4, respectively, and the crystallinity values ranged from 88-91%. The size and morphology of A. tequilana CNC strongly depends on the acid type and hydrolysis time. The shortest CNC obtained with H2SO4 (65 wt%, 40 °C, and 70 min) had a length of 137 ± 68 nm, width 33 ± 7 nm, and height 9.1 nm, whereas the shortest CNC obtained with HCl (2 N, 50 °C and 30 min) had a length of 216 ± 73 nm, width 69 ± 17 nm, and height 8.9 nm. In general, the obtained CNC had an ellipsoidal shape, whereas CNC prepared from H2SO4 were shorter and thinner than those obtained with HCl. The total sulfate group content of CNC obtained with H2SO4 increased with time, temperature, and acid concentration, exhibiting an exponential behavior of CSG=aebt.

| S-EPMC7922795 | biostudies-literature

Cellulose Nanocrystals Derived from Textile Waste through Acid Hydrolysis and Oxidation as Reinforcing Agent of Soy Protein Film.

Project description:More than 10 million tons of textile waste are disposed through landfill every year in North America. The disposal of textile waste via landfill or incineration causes environmental problems and represents a waste of useful resources. In this work, we explored the possibility to directly extract cellulose nanocrystals (CNCs) from untreated textile waste through two methods, namely sulfuric acid hydrolysis and three-step oxidization. CNCs with cellulose I? crystalline structure and rod-like shape were successfully obtained. The aspect ratios of CNCs prepared from acid hydrolysis and oxidization were 10.00 ± 3.39 and 17.10 ± 12.85, respectively. Their application as reinforcing agent of soybean protein isolate (SPI) film was evaluated. With the addition of 20% CNCs, the composite film maintained the high transparency, while their water vapor barrier property, tensile strength, and Young's modulus were significantly improved. This research demonstrates a promising approach to recycle textile waste, and more value-added applications based on the derived CNCs could be expected.

| S-EPMC7240655 | biostudies-literature

Thermochemical hydrolysis of macroalgae Ulva for biorefinery: Taguchi robust design method.

Project description:Understanding the impact of all process parameters on the efficiency of biomass hydrolysis and on the final yield of products is critical to biorefinery design. Using Taguchi orthogonal arrays experimental design and Partial Least Square Regression, we investigated the impact of change and the comparative significance of thermochemical process temperature, treatment time, %Acid and %Solid load on carbohydrates release from green macroalgae from Ulva genus, a promising biorefinery feedstock. The average density of hydrolysate was determined using a new microelectromechanical optical resonator mass sensor. In addition, using Flux Balance Analysis techniques, we compared the potential fermentation yields of these hydrolysate products using metabolic models of Escherichia coli, Saccharomyces cerevisiae wild type, Saccharomyces cerevisiae RN1016 with xylose isomerase and Clostridium acetobutylicum. We found that %Acid plays the most significant role and treatment time the least significant role in affecting the monosaccharaides released from Ulva biomass. We also found that within the tested range of parameters, hydrolysis with 121?°C, 30?min 2% Acid, 15% Solids could lead to the highest yields of conversion: 54.134-57.500?gr ethanol kg(-1) Ulva dry weight by S. cerevisiae RN1016 with xylose isomerase. Our results support optimized marine algae utilization process design and will enable smart energy harvesting by thermochemical hydrolysis.

| S-EPMC4904202 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data