A simple method to set the spray properties for flame spray pyrolysis production of nanoparticles

ABSTRACT: The most critical part of the flame spray pyrolysis (FSP) process is the nozzle, since it plays a key role in setting the spray properties. In this study, we developed an approach to adjust the nozzle throat gap size for a desired dispersion gas flow rate and upstream pressure, based on the external size and shape of a two phase external mixing nozzle. An equation was derived and validated by comparing the predicted gas flow rates with the data provided in a commercial nozzle supplier chart. Experiments were also conducted in our lab-scale FSP reactor to test the validity of the predictions. The approach developed here was found to closely predict the gap size necessary to pass the required dispersion gas flow at a desired pressure drop. Error in predictions was found to be less than 3% at an upstream pressure range of 3–10 bars. The isentropic flow assumption for perfect gases across the convergent-divergent nozzle was found to fail below 2 bars, consistent with the theory applied. By using the method here, the nozzle setting for a desired operation in an FSP process can be easily done, minimizing the time-consuming trial and error steps needed otherwise. Chemical engineering; Nanotechnology; Chemical reaction engineering; Fluid mechanics; Materials synthesis; Flame spray pyrolysis; Nanoparticles; Two phase nozzles; Nozzle gap; Pressure drop.

SUBMITTER: Alhaleeb M

PROVIDER: S-EPMC7509832 | biostudies-literature | 2020 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

The gas-phase formation of tin dioxide nanoparticles in single droplet combustion and flame spray pyrolysis.

Project description:Tin dioxide (SnO2) nanoparticles synthesized via flame spray pyrolysis (FSP) have promising applications for gas sensors. The formation of SnO2 nanoparticles in the gas-phase has been investigated using single droplet combustion and FSP. Precursor solutions of Tin (II) 2-ethylhexanoate dissolved in Xylene with varying Sn concentrations were selected as the precursor-solvent system. The selected precursor-solvent system has its stability and ability to synthesize homogeneous nanoparticles, compared to metal nitrate based precursor solutions. The precursor-solvent system was studied using attenuated total reflection Fourier transform infrared (ATR-FTIR) spectroscopy and thermogravimetric analysis (TGA). The SnO2 nanoparticles were characterized using X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET), and transmission electron microscopy (TEM). Droplet surface micro-explosions were observed during the single droplet combustion of the precursor solutions. It is because of the heterogeneous vapor-phase nucleation, which is beneath the liquid droplet surface and caused by precursor thermal decomposition. The results show that the size of nanoparticles obtained both from FSP and single droplet combustion increases with increasing metal-precursor concentration. The TEM images of the particles from such droplet combustion reveal two types of nanoparticles with different sizes and morphologies. The current work provides fundamental understanding of precursor decomposition and particle formation during single droplet combustion, which help in-depth understanding of the flame spray pyrolysis.

| S-EPMC7116032 | biostudies-literature

Flame Spray Pyrolysis Co3O4/CoO as Highly-Efficient Nanocatalyst for Oxygen Reduction Reaction.

Project description:The oxygen reduction reaction (ORR) is the rate-limiting reaction in the cathode side of fuel cells. In the quest for alternatives to Pt-electrodes as cathodes in ORR, appropriate transition metal oxide-based electrocatalysts are needed. In the present work, we have synthesized Co3O4 and CoO/Co3O4 nanostructures using flame spray pyrolysis (FSP), as electrocatalysts for ORR in acidic and alkaline media. A detailed study of the effect of (Co-oxide)/Pt ratio on ORR efficiency shows that the present FSP-made Co-oxides are able to perform ORR at very low-Pt loading, 0.4% of total metal content. In acid medium, an electrode with (5.2% Pt + 4.8% Co3O4), achieved the highest ORR performance (Jmax = 8.31 mA/cm2, E1/2 = 0.66 V). In alkaline medium, superior performance and stability have been achieved by an electrode with (0.4%Pt + 9.6% (CoO/Co3O4)) with ORR activity (Jmax = 3.5 mA/cm2, E1/2 = 0.08 V). Using XRD, XPS, Raman and TEM data, we discuss the structural and electronic aspects of the FSP-made Co-oxide catalysts in relation to the ORR performance. Cyclic voltammetry data indicate that the ORR process involves active sites associated with Co3+ cations at the cobalt oxide surface. Technology-wise, the present work demonstrates that the developed FSP-protocols, constitutes a novel scalable process for production of co-oxides appropriate for oxygen reduction reaction electrodes.

| S-EPMC8066371 | biostudies-literature

Flame Spray Pyrolysis Synthesis of Vo-Rich Nano-SrTiO<sub>3-x</sub>.

Project description:Engineering of oxygen vacancies (Vo) in nanomaterials allows diligent control of their physicochemical properties. SrTiO3 possesses the typical ABO3 structure and has attracted considerable attention among the titanates due to its chemical stability and its high conduction band energy. This has resulted in its extensive use in photocatalytic energy-related processes, among others. Herein, we introduce the use of Flame Spray Pyrolysis (FSP); an industrial and scalable process to produce Vo-rich SrTiO3 perovskites. We present two types of Anoxic Flame Spray Pyrolysis (A-FSP) technologies using CH4 gas as a reducing source: Radial A-FSP (RA-FSP); and Axial A-FSP (AA-FSP). These are used for the control engineering of oxygen vacancies in the SrTiO3-x nanolattice. Based on X-ray photoelectron spectroscopy, Raman and thermogravimetry-differential thermal analysis, we discuss the role and the amount of the Vos in the so-produced nano-SrTiO3-x, correlating the properties of the nanolattice and energy-band structure of the SrTiO3-x. The present work further corroborates the versatility of FSP as a synthetic process and the potential future application of this process to engineer photocatalysts with oxygen vacancies in quantities that can be measured in kilograms.

| S-EPMC10891825 | biostudies-literature

Metal Oxide Quantum Dots Embedded in Silica Matrices Made by Flame Spray Pyrolysis.

Project description:Quantum dots have unique size-dependent properties and promising applications. However, their use in many applications remains hindered by mechanical, thermal, and chemical instability and the lack of viable quantum dot mass-production processes. Embedding quantum dots in matrices such as silica counteracts the instability challenges in some applications while preserving their unique properties and applicability. Here, we synthesize quantum dots of four different metal oxides embedded in a silica matrix in a one-step mass-production process using flame spray pyrolysis.

| S-EPMC8153950 | biostudies-literature

A Perspective on the Flame Spray Synthesis of Photocatalyst Nanoparticles.

Project description:The synthesis of functional nanoparticles via one-step flame spray pyrolysis (FSP), especially those of catalytic nature, has attracted the interests of scientists and engineers, as well as industries. The rapid and high temperature continuous synthesis yields nanoparticles with intrinsic features of active catalysts, that is, high surface area and surface energetics. For these reasons, FSP finds applications in various thermally inducible catalytic reactions. However, the design and synthesis of photocatalysts by FSP requires a knowledge set which is different from that established for thermal catalysts. Unknown to many, this has resulted in frustrations to those entering the field unprepared, especially since FSP appears to be an elegant tool in synthesising oxide nanoparticles of any elemental construct. From simple oxide to doped-oxide, and mixed metal oxide to the in situ deposition of noble metals, this Perspective gives an overview on the development of photocatalysts made by FSP in the last decade that led to a better understanding of the design criteria. Various challenges and opportunities are also highlighted, especially those beyond simple metal oxides, which perhaps contain the greatest potential for the exploitation of photocatalysts design by FSP.

| S-EPMC5521242 | biostudies-other

Electrical Properties of CZO Films Prepared by Ultrasonic Spray Pyrolysis.

Project description:CuZnO (CZO) films have attracted increasing amounts of attention due to their promising potential applications in semiconductor devices. ZnO shows n-type conductivity, and attempts have been made to dope several elements in ZnO to improve the electrical properties. This study investigated the electrical property transitions of CZO films and determined the copper concentration at which the conductivity of CZO films will change from n-type to p-type. In this study, CZO films were fabricated by ultrasonic spray pyrolysis with copper acetate, zinc acetate, and ammonium acetate precursor solution. The concentrations of Cu ions in the CZO films were controlled by the concentration ratios of copper acetate to zinc acetate in the precursor solutions. In addition, these samples were analyzed by Hall effect measurements, X-ray diffraction, transmittance measurements, and photoluminescence measurements. The results show that the conductivity of the CZO film changes from n-type to p-type when the copper ion concentration in the film is 5%.

| S-EPMC5512636 | biostudies-other

Lattice Defects Engineering in W-, Zr-doped BiVO4 by Flame Spray Pyrolysis: Enhancing Photocatalytic O2 Evolution.

Project description:A flame spray pyrolysis (FSP) method has been developed, for controlled doping of BiVO4 nanoparticles with W and Zr in tandem with the oxygen vacancies (Vo) of the BiVO4 lattice. Based on XPS and Raman data, we show that the nanolattice of W-BiVO4 and Zr-BiO4 can be controlled to achieve optimal O2 evolution from H2O photocatalysis. A synergistic effect is found between the W- and Zr-doping level in correlation with the Vo-concentration. FSP- made W-BiVO4 show optimal photocatalytic O2-production from H2O, up to 1020 μmol/(g × h) for 5%W-BiVO4, while the best performing Zr-doped achieved 970 μmol/(g × h) for 5%Zr-BiVO4. Higher W-or Zr-doping resulted in deterioration in photocatalytic O2-production from H2O. Thus, engineering of FSP-made BiVO4 nanoparticles by precise control of the lattice and doping-level, allows significant enhancement of the photocatalytic O2-evolution efficiency. Technology-wise, the present work demonstrates that flame spray pyrolysis as an inherently scalable technology, allows precise control of the BiVO4 nanolattice, to achieve significant improvement of its photocatalytic efficiency.

| S-EPMC7920441 | biostudies-literature

Electrochemical properties of tungsten sulfide-carbon composite microspheres prepared by spray pyrolysis.

Project description:Tungsten sulfide (WS2)-carbon composite powders with superior electrochemical properties are prepared by a two-step process. WO3-carbon composite powders were first prepared by conventional spray pyrolysis, and they were then sulfidated to form WS2-carbon powders. Bare WS2 powders are also prepared by sulfidation of bare WO3 powders obtained by spray pyrolysis. Stacked graphitic layers could not be found in the bare WS2 and WS2-carbon composite powders. The amorphous bare WS2 and WS2-carbon composite powders have Brunauer-Emmett-Teller (BET) surface areas of 2.8 and 4 m(2) g(-1), respectively. The initial discharge and charge capacities of the WS2-carbon composite powders at a current density of 100 mA g(-1) are 1055 and 714 mA h g(-1), respectively, and the corresponding initial Coulombic efficiency is 68%. On the other hand, the initial discharge and charge capacities of the bare WS2 powders are 514 and 346 mA h g(-1), respectively. The discharge capacities of the WS2-carbon composite powders for the 2(nd) and 50(th) cycles are 716 and 555 mA h g(-1), respectively, and the corresponding capacity retention measured after first cycle is 78%.

| S-EPMC4148672 | biostudies-literature

Inverted Perovskite Photovoltaics Using Flame Spray Pyrolysis Solution Based CuAlO<sub>2</sub>/Cu-O Hole-Selective Contact.

Project description:We present the functionalization process of a conductive and transparent CuAlO2/Cu-O hole-transporting layer (HTL). The CuAlO2/Cu-O powders were developed by flame spray pyrolysis and their stabilized dispersions were treated by sonication and centrifugation methods. We show that when the supernatant part of the treated CuAlO2/Cu-O dispersions is used for the development of CuAlO2/Cu-O HTLs the corresponding inverted perovskite-based solar cells show improved functionality and power conversion efficiency of up to 16.3% with negligible hysteresis effect.

| S-EPMC6543770 | biostudies-literature

Effect of AuPd Bimetal Sensitization on Gas Sensing Performance of Nanocrystalline SnO2 Obtained by Single Step Flame Spray Pyrolysis.

Project description:Improvement of sensitivity, lower detection limits, stability and reproducibility of semiconductor metal oxide gas sensor characteristics are required for their application in the fields of ecological monitoring, industrial safety, public security, express medical diagnostics, etc. Facile and scalable single step flame spray pyrolysis (FSP) synthesis of bimetal AuPd sensitized nanocrystalline SnO2 is reported. The materials chemical composition, structure and morphology has been studied by XRD, XPS, HAADFSTEM, BET, ICP-MS techniques. Thermo-programmed reduction with hydrogen (TPR-H2) has been used for materials chemical reactivity characterization. Superior gas sensor response of bimetallic modified SnO2 towards wide concentration range of reducing (CO, CH4, C3H8, H2S, NH3) and oxidizing (NO2) gases compared to pure and monometallic modified SnO2 is reported for dry and humid gas detection conditions. The combination of facilitated oxygen molecule spillover on gold particles and electronic effect of Fermi level control by reoxidizing Pd-PdO clusters on SnO2 surface is proposed to give rise to the observed enhanced gas sensor performance.

| S-EPMC6567076 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data