Magnetic, Electronic, and Mechanical Properties of Bulk ε-Fe₂N Synthesized at High Pressures.

ABSTRACT: We sintered bulk trigonal ε-Fe₂N (space group: P312) with the high-pressure and high-temperature method. Structural refinements by the Rietveld method result in a trigonal unit cell with parameters of a = 4.7767(1) Å and c = 4.4179(3) Å. ε-Fe₂N is ferromagnetic with a Curie temperature of ∼250 K, a saturation magnetization (M _s) value of up to 1.2 μ_B/formula units (f.u.), and comparatively low coercive field. The Vickers hardness was measured, and the results showed that the asymptotic hardness of bulk ε-Fe₂N is about 6.5 GPa with a load of 1000 g. Thermogravimetric (TG) analysis shows that ε-Fe₂N is thermally stable below 670 K. ε-Fe₂N exhibits good metal conductivity, and the electron transport measurements show that the resistivity of it is 172 μΩ cm at room temperature. The theoretical calculations suggest that the conducting states are mainly derive from Fe-3d states.

SUBMITTER: Ma T

PROVIDER: S-EPMC8154168 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Background: Minimally invasive modalities are of great interest in the field of treating bone tumors. However, providing reliable mechanical support and fast killing of tumor cells to achieve rapid recovery of physical function is still challenging in clinical works. Methods: A material with two functions, mechanical support and magnetic thermal ablation, was developed from Fe3O4 nanoparticles (NPs) distributed in a polymethylmethacrylate (PMMA) bone cement. The mechanical properties and efficiency of magnetic field-induced thermal ablation were systematically and successfully evaluated in vitro and ex vivo. CT images and pathological examination were successfully applied to evaluate therapeutic efficacy with a rabbit bone tumor model. Biosafety evaluation was performed with a rabbit in vivo, and a cytotoxicity test was performed in vitro. Results: An NP content of 6% Fe3O4 (PMMA-6% Fe3O4, mFe: 0.01 g) gave the most suitable performance for in vivo study. At the 56-day follow-up after treatment, bone tumors were ablated without obvious side effects. The pathological examination and new bone formation in CT images clearly illustrate that the bone tumors were completely eliminated. Correspondingly, after treatment, the tendency of bone tumors toward metastasis significantly decreased. Moreover, with well-designed mechanical properties, PMMA-6%Fe3O4 implantation endowed tumor-bearing rabbit legs with excellent bio-mimic bone structure and internal support. Biosafety evaluation did not induce an increase or decrease in the immune response, and major functional parameters were all at normal levels. Conclusion: We have presented a novel, highly efficient and minimally invasive approach for complete bone tumor regression and bone defect repair by magnetic thermal ablation based on PMMA containing Fe3O4 NPs; this approach shows excellent heating ability for rabbit VX2 tibial plateau tumor ablation upon exposure to an alternating magnetic field (AMF) and provides mechanical support for bone repair. The new and powerful dual-function implant is a promising minimally invasive agent for the treatment of bone tumors and has good clinical translation potential.

Dataset Information

Magnetic, Electronic, and Mechanical Properties of Bulk ε-Fe₂N Synthesized at High Pressures.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets

Dataset Information

Magnetic, Electronic, and Mechanical Properties of Bulk ε-Fe2N Synthesized at High Pressures.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets

Magnetic, Electronic, and Mechanical Properties of Bulk ε-Fe₂N Synthesized at High Pressures.