Cefotaxime removal enhancement via bio-nanophotocatalyst α-Fe₂O₃ using photocatalytic degradation technique and its echo-biomedical applications.

ABSTRACT: The present paper evaluates the photocatalytic degradation (PCD) performance of the biofabricated hematite nanoparticles (α-HNPs) for the degradation approach of the Cefotaxime (Cfm). The optimum pH of the solution to achieve the best PCD was found to be 10.5. The kinetics study for the PCD of the Cfm via α-HNPs has been investigated and the reaction was found to be fellow pseudo-first-order at R² = 0.992. The mass loading impact of α-HNPs was investigated and estimated for the maximum degradation of Cfm 0.4 mg/mL. UV-Vis confirmed that α-HNPs had a direct transition bandgap at 3.78 eV at a maximum absorption wavelength of 362 nm with suspension stability for 7 days. The probable mechanism of the Cfm PCD via α-HNPs and the degradation pathway was conducted. The validation of the suspension stability of the α-HNPs (-68.6 ± 11.8 mV) was determined using the zeta potential investigation test. XRD investigation was conducted after Cfm PCD showing an average crystallite size of 27.0 nm. XRD, TEM, SEM, EDX, and FT-IR analyses have been conducted for the α-HNPs before and after Cfm PCD confirming the high efficiency for the reusability of the current biocatalyst α-HNPs for further use. TEM results of the particle sizes of α-HNPs were found at 19.2 ± 4.4 and 20.6 ± 7.4 nm respectively before and after Cfm PCD. The efficiency of the Cfm PCD was found to be 99.1% after 6 h. High potent as an antibacterial agent of α-HNPs was investigated either α-HNPs alone or after its PCD activity against Cfm. The antibacterial activity revealed high sensitivity, especially toward Gram-positive species indicating its promising ability against pathogenic issues. Interestingly, Cfm@α-HNPs showed superior anti-proliferative activity as tested by MTT assay and were able to induce apoptosis in MCF7 and HepG2 cell lines using the flow cytometry technique at 20.7% and 17% respectively. Also, The IC₅₀ of hydrogen peroxide scavenging was estimated and it was manifested that 635.8 and 665.6 μg/mL of α-HNPs before and after the PCD process of Cfm respectively.

SUBMITTER: Al-Hakkani MF

PROVIDER: S-EPMC9279508 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:By photodeposition of CrOx on SrTiO3-based semiconductors doped with aliovalent Mg(II) and functionalized with Ni/NiOx catalytic nanoparticles (economically significantly more viable than commonly used Rh catalysts), an increase in apparent quantum yield (AQYs) from ∼10 to 26% in overall water splitting was obtained. More importantly, deposition of CrOx also significantly enhances the stability of Ni/NiO nanoparticles in the production of hydrogen, allowing sustained operation, even in intermittent cycles of illumination. In situ elemental analysis of the water constituents during or after photocatalysis by inductively coupled plasma mass spectrometry/optical emission spectrometry shows that after CrOx deposition, dissolution of Ni ions from Ni/NiOx-Mg:SrTiO3 is significantly suppressed, in agreement with the stabilizing effect observed, when both Mg dopant and CrOx are present. State-of-the-art electron microscopy and energy-dispersive X-ray spectroscopy (EDX) and electron energy-loss spectroscopy (EELS) analyses demonstrate that upon preparation, CrOx is photodeposited in the vicinity of several, but not all, Ni/NiOx particles. This implies the formation of a Ni-Cr mixed metal oxide, which is highly effective in water reduction. Inhomogeneities in the interfacial contact, evident from differences in contact angles between Ni/NiOx particles and the Mg:SrTiO3 semiconductor, likely affect the probability of reduction of Cr(VI) species during synthesis by photodeposition, explaining the observed inhomogeneity in the spatial CrOx distribution. Furthermore, by comparison with undoped SrTiO3, Mg-doping appears essential to provide such favorable interfacial contact and to establish the beneficial effect of CrOx. This study suggests that the performance of semiconductors can be significantly improved if inhomogeneities in interfacial contact between semiconductors and highly effective catalytic nanoparticles can be resolved by (surface) doping and improved synthesis protocols.

Dataset Information

Cefotaxime removal enhancement via bio-nanophotocatalyst α-Fe₂O₃ using photocatalytic degradation technique and its echo-biomedical applications.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets

Dataset Information

Cefotaxime removal enhancement via bio-nanophotocatalyst α-Fe2O3 using photocatalytic degradation technique and its echo-biomedical applications.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets

Cefotaxime removal enhancement via bio-nanophotocatalyst α-Fe₂O₃ using photocatalytic degradation technique and its echo-biomedical applications.