Enhancement of the Si p-n diode NIR photoresponse by embedding β-FeSi2 nanocrystallites.

ABSTRACT: By using solid phase epitaxy of thin Fe films and molecular beam epitaxy of Si, a p(+)-Si/p-Si/β-FeSi2 nanocrystallites/n-Si(111) diode structure was fabricated. Transmission electron microscopy data confirmed a well-defined multilayered structure with embedded nanocrystallites of two typical sizes: 3-4 and 15-20 nm, and almost coherent epitaxy of the nanocrystallites with the Si matrix. The diode at zero bias conditions exhibited a current responsivity of 1.7 mA/W, an external quantum efficiency of about 0.2%, and a specific detectivity of 1.2 × 10(9) cm × Hz(1/2)/W at a wavelength of 1300 nm at room temperature. In the avalanche mode, the responsivity reached up to 20 mA/W (2% in terms of efficiency) with a value of avalanche gain equal to 5. The data obtained indicate that embedding of β-FeSi2 nanocrystallites into the depletion region of the Si p-n junction results in expansion of the spectral sensitivity up to 1600 nm and an increase of the photoresponse by more than two orders of magnitude in comparison with a conventional Si p-n junction. Thereby, fabricated structure combines advantage of the silicon photodiode functionality and simplicity with near infrared light detection capability of β-FeSi2.

SUBMITTER: Shevlyagin AV

PROVIDER: S-EPMC4593177 | biostudies-other | 2015

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Narrow-Linewidth GaN-on-Si Laser Diode with Slot Gratings.

Project description:This letter reports room-temperature electrically pumped narrow-linewidth GaN-on-Si laser diodes. Unlike conventional distributed Bragg feedback laser diodes with hundreds of gratings, we employed only a few precisely defined slot gratings to narrow the linewidth and mitigate the negative effects of grating fabrication on the device performance. The slot gratings were incorporated into the ridge of conventional Fabry-Pérot cavity laser diodes. A subsequent wet etching in a tetramethyl ammonium hydroxide solution not only effectively removed the damages induced by the dry etching, but also converted the rough and tilted slot sidewalls into smooth and vertical ones. As a result, the threshold current was reduced by over 20%, and the reverse leakage current was decreased by over three orders of magnitude. Therefore, the room-temperature electrically pumped narrow-linewidth GaN-on-Si laser diode has been successfully demonstrated.

| S-EPMC8619470 | biostudies-literature

Hierarchical Si/ZnO trunk-branch nanostructure for photocurrent enhancement.

Project description:Hierarchical Si/ZnO trunk-branch nanostructures (NSs) have been synthesized by hot wire assisted chemical vapor deposition method for trunk Si nanowires (NWs) on indium tin oxide (ITO) substrate and followed by the vapor transport condensation (VTC) method for zinc oxide (ZnO) nanorods (NRs) which was laterally grown from each Si nanowires (NWs). A spin coating method has been used for zinc oxide (ZnO) seeding. This method is better compared with other group where they used sputtering method for the same process. The sputtering method only results in the growth of ZnO NRs on top of the Si trunk. Our method shows improvement by having the growth evenly distributed on the lateral sides and caps of the Si trunks, resulting in pine-leave-like NSs. Field emission scanning electron microscope image shows the hierarchical nanostructures resembling the shape of the leaves of pine trees. Single crystalline structure for the ZnO branch grown laterally from the crystalline Si trunk has been identified by using a lattice-resolved transmission electron microscope. A preliminary photoelectrochemical (PEC) cell testing has been setup to characterize the photocurrent of sole array of ZnO NR growth by both hydrothermal-grown (HTG) method and VTC method on ITO substrates. VTC-grown ZnO NRs showed greater photocurrent effect due to its better structural properties. The measured photocurrent was also compared with the array of hierarchical Si/ZnO trunk-branch NSs. The cell with the array of Si/ZnO trunk-branch NSs revealed four-fold magnitude enhancement in photocurrent density compared with the sole array of ZnO NRs obtain from VTC processes.

| S-EPMC4160322 | biostudies-literature

Signal enhancement in supercritical fluid chromatography-diode-array detection with multiple injection.

Project description:To circumvent the detrimental effects of large-volume injection with fixed-loop injector in modern supercritical fluid chromatography, the feasibility of performing multiple injection was investigated. By accumulating analytes from a certain number of continual small-volume injections, compounds can be concentrated on the column head, and this leads to signal enhancement compared with a single injection. The signal to noise enhancement of different compounds appeared to be associated with their retention on different stationary phases and with type of sample diluent. The diethylamine column gave the best signal to noise enhancement when acetonitrile was used as sample diluent and the 2-picolylamine column showed the best overall performance with water as the sample diluent. The advantage of multiple injection over one-time large-volume injection was proven with sulfanilamide, with both acetonitrile and water as sample diluents. The multiple injection approach exhibited comparable within- and between-day precision of retention time and peak area with those of single injections. The potential of the multiple injection approach was demonstrated in the analysis of sulfanilamide-spiked honey extract and diclofenac-spiked ground water sample. The limitations of this approach were also discussed.

| S-EPMC6972688 | biostudies-literature

Theoretical and Experimental Study on AlGaN/GaN Schottky Barrier Diode on Si Substrate with Double-Heterojunction.

Project description:An AlGaN/GaN Schottky barrier diode (SBD) with double-heterojunction is theoretically and experimentally investigated on the GaN/AlGaN/GaN/Si-sub. The two-dimensional hole gas (2DHG) and electron gas (2DEG) are formed at the GaN-top/AlGaN and AlGaN/GaN interface, respectively. At the off-state, the 2DEH and 2DHG are partially depleted and then completely disappear. There remain the fixed positive and negative polarization charges, forming the polarization junction. Therefore, a flat electric field in the drift region and a high breakdown voltage (BV) are obtained. Moreover, the anode is recessed to reduce turn-on voltage (VON). The low-damage ICP etching process results in the improved Schottky contacts, and a low leakgae current and a low VON is obtained. The fabricated SBD exhibits a BV of 1109?V with anode-to-cathode distance (LAC) of 11??m. The fabricated SBDs achieve a low VON of 0.68?V with good uniformity, a high on/off current ratio ? 1010 at room temperature, a low specific on-resistance (RON,SP) of 1.17 m? cm2, and a high Baliga's figure-of-merit (FOM) of 1051?MW/cm2.

| S-EPMC7364695 | biostudies-literature

Simplified ZrTiO x -based RRAM cell structure with rectifying characteristics by integrating Ni/n?+?-Si diode.

Project description:A simplified one-diode one-resistor (1D1R) resistive switching memory cell that uses only four layers of TaN/ZrTiO x /Ni/n(+)-Si was proposed to suppress sneak current where TaN/ZrTiO x /Ni can be regarded as a resistive-switching random access memory (RRAM) device while Ni/n(+)-Si acts as an Schottky diode. This is the first RRAM cell structure that employs metal/semiconductor Schottky diode for current rectifying. The 1D1R cell exhibits bipolar switching behavior with SET/RESET voltage close to 1 V without requiring a forming process. More importantly, the cell shows tight resistance distribution for different states, significantly rectifying characteristics with forward/reverse current ratio higher than 10(3) and a resistance ratio larger than 10(3) between two states. Furthermore, the cell also displays desirable reliability performance in terms of long data retention time of up to 10(4) s and robust endurance of 10(5) cycles. Based on the promising characteristics, the four-layer 1D1R structure holds the great potential for next-generation nonvolatile memory technology.

| S-EPMC4046995 | biostudies-literature

Highly Fast Response of Pd/Ta2O5/SiC and Pd/Ta2O5/Si Schottky Diode-Based Hydrogen Sensors.

Project description:Herein, the fabrication of a novel highly sensitive and fast hydrogen (H2) gas sensor, based on the Ta2O5 Schottky diode, is described. First, Ta2O5 thin films are deposited on silicon carbide (SiC) and silicon (Si) substrates via a radio frequency (RF) sputtering method. Then, Pd and Ni are respectively deposited on the front and back of the device. The deposited Pd serves as a H2 catalyst, while the Ni functions as an Ohmic contact. The devices are then tested under various concentrations of H2 gas at operating temperatures of 300, 500, and 700 °C. The results indicate that the Pd/Ta2O5 Schottky diode on the SiC substrate exhibits larger concentration and temperature sensitivities than those of the device based on the Si substrate. In addition, the optimum operating temperature of the Pd/Ta2O5 Schottky diode for use in H2 sensing is shown to be about 300 °C. At this optimum temperature, the dynamic responses of the sensors towards various concentrations of H2 gas are then examined under a constant bias current of 1 mA. The results indicate a fast rise time of 7.1 s, and a decay of 18 s, for the sensor based on the SiC substrate.

| S-EPMC7913499 | biostudies-literature

Transparent conductor-embedding nanocones for selective emitters: optical and electrical improvements of Si solar cells.

Project description:Periodical nanocone-arrays were employed in an emitter region for high efficient Si solar cells. Conventional wet-etching process was performed to form the nanocone-arrays for a large area, which spontaneously provides the graded doping features for a selective emitter. This enables to lower the electrical contact resistance and enhances the carrier collection due to the high electric field distribution through a nanocone. Optically, the convex-shaped nanocones efficiently reduce light-reflection and the incident light is effectively focused into Si via nanocone structure, resulting in an extremely improved the carrier collection performances. This nanocone-arrayed selective emitter simultaneously satisfies optical and electrical improvement. We report the record high efficiency of 16.3% for the periodically nanoscale patterned emitter Si solar cell.

| S-EPMC4365400 | biostudies-literature

Room-temperature continuous-wave electrically pumped InGaN/GaN quantum well blue laser diode directly grown on Si.

Project description:Current laser-based display and lighting applications are invariably using blue laser diodes (LDs) grown on free-standing GaN substrates, which are costly and smaller in size compared with other substrate materials.1-3 Utilizing less expensive and large-diameter Si substrates for hetero-epitaxial growth of indium gallium nitride/gallium nitride (InGaN/GaN) multiple quantum well (MQW) structure can substantially reduce the cost of blue LDs and boost their applications. To obtain a high crystalline quality crack-free GaN thin film on Si for the subsequent growth of a blue laser structure, a hand-shaking structure was formed by inserting Al-composition step down-graded AlN/AlxGa1-xN buffer layers between GaN and Si substrate. Thermal degradation in InGaN/GaN blue MQWs was successfully suppressed with indium-rich clusters eliminated by introducing hydrogen during the growth of GaN quantum barriers (QBs) and lowering the growth temperature for the p-type AlGaN/GaN superlattice optical cladding layer. A continuous-wave (CW) electrically pumped InGaN/GaN quantum well (QW) blue (450 nm) LD grown on Si was successfully demonstrated at room temperature (RT) with a threshold current density of 7.8 kA/cm2.

| S-EPMC6106987 | biostudies-literature

NIR self-powered photodetection and gate tunable rectification behavior in 2D GeSe/MoSe<sub>2</sub> heterojunction diode.

Project description:Two-dimensional (2D) heterostructure with atomically sharp interface holds promise for future electronics and optoelectronics because of their multi-functionalities. Here we demonstrate gate-tunable rectifying behavior and self-powered photovoltaic characteristics of novel p-GeSe/n-MoSe2 van der waal heterojunction (vdW HJ). A substantial increase in rectification behavior was observed when the devices were subjected to gate bias. The highest rectification of ~ 1 × 104 was obtained at Vg = - 40 V. Remarkable rectification behavior of the p-n diode is solely attributed to the sharp interface between metal and GeSe/MoSe2. The device exhibits a high photoresponse towards NIR (850 nm). A high photoresponsivity of 465 mAW-1, an excellent EQE of 670%, a fast rise time of 180 ms, and a decay time of 360 ms were obtained. Furthermore, the diode exhibits detectivity (D) of 7.3 × 109 Jones, the normalized photocurrent to the dark current ratio (NPDR) of 1.9 × 1010 W-1, and the noise equivalent power (NEP) of 1.22 × 10-13 WHz-1/2. The strong light-matter interaction stipulates that the GeSe/MoSe2 diode may open new realms in multi-functional electronics and optoelectronics applications.

| S-EPMC7878902 | biostudies-literature

Irradiation induced fluorescence enhancement in PEGylated cyanine-based NIR nano- and mesoscale GUMBOS.

Project description:We report on the synthesis and characterization of a PEGylated IR786 GUMBOS (Group of Uniform Materials Based on Organic Salts). The synthesis of this material was accomplished using a three step protocol: (1) substitution of chloride on the cyclohexenyl ring in the heptamethine chain of IR786 by 6-aminohexanoic acid, (2) grafting of methoxy polyethylene glycol (MeOPEG) onto the 6-aminohexanoic acid via an esterification reaction, and (3) anion exchange between [PEG786][I] and lithium bis(trifluoromethylsulfonyl)imide (LiNTf(2)) or sodium bis(2-ethylhexyl)sulfosuccinate (AOT) in order to obtain PEG786 GUMBOS. Examination of spectroscopic data for this PEG786 GUMBOS indicates a large stokes shift (122 nm). It was observed that this PEG786 GUMBOS associates in aqueous solution to form nano- and mesoscale self-assemblies with sizes ranging from 100 to 220 nm. These nano- and mesoscale GUMBOS are also able to resist nonspecific binding to proteins. PEGylation of the original IR786 leads to reduced cytotoxicity. In addition, it was noted that anions, such as NTf(2) and AOT, play a significant role in improving the photostability of PEG786 GUMBOS. Irradiation-induced J-aggregation in [PEG786][NTf(2)] and to some extent in [PEG786][AOT] produced enhanced photostability. This observation was supported by use of both steady state and time-resolved fluorescence measurements.

| S-EPMC4172377 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data