Outstanding supercapacitive properties of Mn-doped TiO2 micro/nanostructure porous film prepared by anodization method.

ABSTRACT: Mn-doped TiO2 micro/nanostructure porous film was prepared by anodizing a Ti-Mn alloy. The film annealed at 300 °C yields the highest areal capacitance of 1451.3 mF/cm(2) at a current density of 3 mA/cm(2) when used as a high-performance supercapacitor electrode. Areal capacitance retention is 63.7% when the current density increases from 3 to 20 mA/cm(2), and the capacitance retention is 88.1% after 5,000 cycles. The superior areal capacitance of the porous film is derived from the brush-like metal substrate, which could greatly increase the contact area, improve the charge transport ability at the oxide layer/metal substrate interface, and thereby significantly enhance the electrochemical activities toward high performance energy storage. Additionally, the effects of manganese content and specific surface area of the porous film on the supercapacitive performance were also investigated in this work.

SUBMITTER: Ning X

PROVIDER: S-EPMC4778052 | biostudies-other | 2016

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

One-step Synthesis of Ordered Pd@TiO2 Nanofibers Array Film as Outstanding NH3 Gas Sensor at Room Temperature.

Project description:The one dimensional (1D) ordered porous Pd@TiO2 nanofibers (NFs) array film have been fabricated via a facile one-step synthesis of the electrospinning approach. The Pd@TiO2 NFs (PTND3) contained Pd (2.0 wt %) and C, N element (16.2 wt %) display high dispersion of Pd nanoparticles (NPs) on TiO2 NFs. Adding Pd meshed with C, N element to TiO2 based NFs might contribute to generation of Lewis acid sites and Brønsted acid sites, which have been recently shown to enhance NH3 adsorption-desorption ability; Pd NPs could increase the quantity of adsorbed O2 on the surface of TiO2 based NFs, and accelerated the O2 molecule-ion conversion rate, enhanced the ability of electron transmission. The response time of PTND3 sensor towards 100 ppm NH3 is only 3 s at room temperature (RT). Meantime, the response and response time of the PTND3 to the NH3 is 1 and 14s even at the concentration of 100 ppb. Therefore, the ordered Pd@TiO2 NFs array NH3 sensor display great potential for practical applications.

| S-EPMC5677023 | biostudies-literature

Tantalum-Doped TiO2 Prepared by Atomic Layer Deposition and Its Application in Perovskite Solar Cells.

Project description:Tantalum (Ta)-doped titanium oxide (TiO2) thin films are grown by plasma enhanced atomic layer deposition (PEALD), and used as both an electron transport layer and hole blocking compact layer of perovskite solar cells. The metal precursors of tantalum ethoxide and titanium isopropoxide are simultaneously injected into the deposition chamber. The Ta content is controlled by the temperature of the metal precursors. The experimental results show that the Ta incorporation introduces oxygen vacancies defects, accompanied by the reduced crystallinity and optical band gap. The PEALD Ta-doped films show a resistivity three orders of magnitude lower than undoped TiO2, even at a low Ta content (0.8-0.95 at.%). The ultraviolet photoelectron spectroscopy spectra reveal that Ta incorporation leads to a down shift of valance band and conduction positions, and this is helpful for the applications involving band alignment engineering. Finally, the perovskite solar cell with Ta-doped TiO2 electron transport layer demonstrates significantly improved fill factor and conversion efficiency as compared to that with the undoped TiO2 layer.

| S-EPMC8226548 | biostudies-literature

Outstanding Photoluminescence in Pr3+-Doped Perovskite Ceramics.

Project description:Ba (Zr0.2Ti0.8) O?-50% (Ba0.7Ca0.3) TiO? (BZT-0.5BCT) ceramics with different doping contents of Pr3+ were prepared by the conventional solid-state reaction. The phase structure and crystallinity of the fabricated ceramics were investigated by X-ray diffraction, Raman spectroscopy, and scanning electron microscopy. Photoluminescence (PL) emission spectra were measured to analyze the PL characteristics. The strong intensities of a green band at 489 nm and a red band at 610 nm were observed. The maximum emission intensity of the PL spectrum was achieved in the BZT-0.5BCT ceramic with 0.2% mol of Pr3+ ions. Furthermore, the PL spectra of BZT-0.5BCT ceramics were found to be sensitive to polarization of the ferroelectric ceramics. Compared with the unpoled ceramics, the green emission increased about 42% and a new emission peak at 430 nm appeared for the poled ceramics. With excellent intrinsic ferroelectricity and an enhanced PL property, such material has potential to realize multifunctionality in a wide application range.

| S-EPMC6187377 | biostudies-other

Hierarchical TiO2 Layers Prepared by Plasma Jets.

Project description:Heterogeneous photocatalysis of TiO2 is one of the most efficient advanced oxidation processes for water and air purification. Here, we prepared hierarchical TiO2 layers (Spikelets) by hollow-cathode discharge sputtering and tested their photocatalytic performance in the abatement of inorganic (NO, NO2) and organic (4-chlorophenol) pollutant dispersed in air and water, respectively. The structural-textural properties of the photocatalysts were determined via variety of physico-chemical techniques (XRD, Raman spectroscopy, SEM, FE-SEM. DF-TEM, EDAX and DC measurements). The photocatalysis was carried out under conditions similar to real environment conditions. Although the abatement of NO and NO2 was comparable with that of industrial benchmark Aeroxide® TiO2 P25, the formation of harmful nitrous acid (HONO) product on the Spikelet TiO2 layers was suppressed. Similarly, in the decontamination of water by organics, the mineralization of 4-chlorophenol on Spikelet layers was interestingly the same, although their reaction rate constant was three-times lower. The possible explanation may be the more than half-magnitude order higher external quantum efficacy (EQE) compared to that of the reference TiO2 P25 layer. Therefore, such favorable kinetics and reaction selectivity, together with feasible scale-up, make the hierarchical TiO2 layers very promising photocatalyst which can be used for environmental remediation.

| S-EPMC8706491 | biostudies-literature

Heteroatom-doped highly porous carbons prepared by <i>in situ</i> activation for efficient adsorptive removal of sulfamethoxazole.

Project description:Using organic salts as precursors, heteroatom-doped porous carbons prepared by in situ activation had surface areas of up to 2703 m2 g-1. These porous carbons have been found to be effective adsorbents for adsorption of sulfamethoxazole (SMX) from water. The effects of precursor type, calcination temperature, pH and ionic strength as well as the regeneration properties were investigated. The different adsorption performances of porous carbons were related to their textural structures and chemical properties, and a reasonable adsorption mechanism was proposed. The effects of different heteroatom functional groups on the adsorption of SMX were also analyzed in detail. For potential practical applications, the performance of the porous carbon for removing SMX from real water was also tested.

| S-EPMC9047560 | biostudies-literature

Gradient control of the adhesive force between Ti/TiO2 nanotubular arrays fabricated by anodization.

Project description:The poor control of the adhesion of TiO2 nanotubes (TNTs) layers to a non-anodized titanium (Ti) substrate has limited their widespread application, because the stripping mechanism has not yet been revealed. Here, we report a novel method to control the detachment of TNTs by post-treatment of the as-fabricated samples in protic and aprotic solvents with different polarities. Post-treatment using an organic solvent of lower polarity increases the adhesion of the tube layer, in contrast to the spontaneous detachment of the TNT layer after treatment using a solvent of higher polarity. The structure and the composition at the rupture interface were studied to explore the mechanism of the stripping behavior. Based on our experimental results and previous studies, a hypothesis of a hydrogen-assisted cracking (HAC) mechanism was proposed to explain the mechanism of TNTs' natural detachment and the control over of TNTs' stripping behaviors by post-treatment, in which the presence of protons at the interface between the TNT layer and the Ti substrate play an important role in controlling the two layers' cohesion. In summary, this method and mechanism hold promise to be used as a tool for the design and fabrication of TNT-related materials in future.

| S-EPMC4241524 | biostudies-literature

Micro/Nano hierarchical peony-like Al doped ZnO superhydrophobic film: The guiding effect of (100) preferred seed layer.

Project description:In this communication, we present a versatile and controllable strategy for formation of superhydrophobic micro/nano hierarchical Al doped ZnO (AZO) films with a water contact angle (CA) of 170?±?4°. This strategy involves a two-step layer-by-layer process employing an atomic layer deposition (ALD) technique followed by a hydrothermal method, and the resulting novel AZO surface layer consists of (100) dominant nano-rice-like AZO seed layer (the water CA of 110?±?4°) covered with micro-peony-like AZO top. The growth mechanisms and superhydrophobic properties of the hierarchical AZO layer are discussed. It is believed that the present route holds promise for future success in the design and development of practical superhydrophobic materials.

| S-EPMC4709682 | biostudies-literature

The effect of ethylene glycol on pore arrangement of anodic aluminium oxide prepared by hard anodization.

Project description:The influence of the addition of ethylene glycol (EG) on the pore self-ordering process in anodic aluminium oxide (AAO) membranes prepared by hard anodization (HA) was investigated. It was illustrated that EG has a substantial effect on the pore arrangement of AAO, and it was found that a smaller pore size can be obtained with an EG concentration reaching 20?wt% in aqueous electrolyte. The number of estimated defects of AAO increases significantly with an increase in EG concentration to 50?wt%. Excellent ordering of pores was realized when the samples were anodized in the 30?wt%-EG-containing aqueous electrolyte.

| S-EPMC5882678 | biostudies-literature

Synthesis of MnO/C/NiO-Doped Porous Multiphasic Composites for Lithium-Ion Batteries by Biomineralized Mn Oxides from Engineered Pseudomonas putida Cells.

Project description:A biotemplated cation-incoporating method based on bacterial cell-surface display technology and biogenic Mn oxide mineralization process was developed to fabricate Mn-based multiphasic composites as anodes for Li-ion batteries. The engineered Pseudomonas putida MB285 cells with surface-immobilized multicopper oxidase serve as nucleation centers in the Mn oxide biomineralization process, and the Mn oxides act as a settler for incorporating Ni ions to form aggregates in this process. The assays using X-ray photoelectron spectroscopy, phase compositions, and fine structures verified that the resulting material MnO/C/NiO (CMB-Ni) was porous multiphasic composites with spherical and porous nanostructures. The electrochemical properties of materials were improved in the presence of NiO. The reversible discharge capacity of CMB-Ni remained at 352.92 mAh g-1 after 200 cycles at 0.1 A g-1 current density. In particular, the coulombic efficiency was approximately 100% after the second cycle for CMB-Ni.

| S-EPMC7912735 | biostudies-literature

Hybrid TiO2-ZnO Nanomaterials Prepared Using Laser Ablation in Liquid.

Project description:Hybrids of semiconductor nanomaterials often demonstrate properties that are superior to those of their components. In this study, we prepared hybrid nanomaterials of TiO2 and ZnO, which are among the most actively studied semiconductors, by means of millisecond-pulsed laser and analyzed how their morphology, particle size, and surface composition depend on preparation conditions. A series of nanomaterials were obtained via sequentially ablating Zn and Ti metal plates (in different sequences) in water, while laser pulses of lower (2.0 J/pulse) and higher (5.0 J/pulse) energy were applied. The properties of laser-produced hybrid TiO2-ZnO nanomaterials were shown to be governed by experimental conditions such as laser pulse width, pulse peak power, and reaction media (either pure water or colloid with nanoparticles). The morphology revealed nanospheres of TiO2 that decorate nanorods of ZnO or flower-like aggregates of zinc oxide. Intriguingly, after extended ablation time, titania was found to be self-doped with Ti3+ and Ti2+ ions, and the contribution of lower oxidation states of titanium could be controlled by the applied laser pulse energy. The physicochemical characteristics of hybrid nanomaterials were compared with pure ZnO and TiO2 prepared under the same laser conditions.

| S-EPMC7040934 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data