Crack nucleation criterion and its application to impact indentation in glasses.

ABSTRACT: Molecular dynamics (MD) simulations are used to directly observe nucleation of median cracks in oxide glasses under indentation. Indenters with sharp angles can nucleate median cracks in samples with no pre-existing flaws, while indenters with larger indenter angles cannot. Increasing the tip radius increases the critical load for nucleation of the median crack. Based upon an independent set of simulations under homogeneous loading, the fracture criterion in the domain of the principal stresses is constructed. The fracture criterion, or "fracture locus", can quantitatively explain the observed effects of indenter angle and indenter tip radius on median crack nucleation. Our simulations suggest that beyond the maximum principal stress, plasticity and multi-axial stresses should also be considered for crack nucleation under indentation, even for brittle glassy systems.

SUBMITTER: Luo J

PROVIDER: S-EPMC4832188 | biostudies-other | 2016 Apr

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Shear-banding Induced Indentation Size Effect in Metallic Glasses.

Project description:Shear-banding is commonly regarded as the "plasticity carrier" of metallic glasses (MGs), which usually causes severe strain localization and catastrophic failure if unhindered. However, through the use of the high-throughput dynamic nanoindentation technique, here we reveal that nano-scale shear-banding in different MGs evolves from a "distributed" fashion to a "localized" mode when the resultant plastic flow extends over a critical length scale. Consequently, a pronounced indentation size effect arises from the distributed shear-banding but vanishes when shear-banding becomes localized. Based on the critical length scales obtained for a variety of MGs, we unveil an intrinsic interplay between elasticity and fragility that governs the nanoscale plasticity transition in MGs. Our current findings provide a quantitative insight into the indentation size effect and transition mechanisms of nano-scale plasticity in MGs.

| S-EPMC4914989 | biostudies-literature

Crack-resistant Al2O3-SiO2 glasses.

Project description:Obtaining "hard" and "crack-resistant" glasses have always been of great important in glass science and glass technology. However, in most commercial glasses both properties are not compatible. In this work, colorless and transparent xAl2O3-(100-x)SiO2 glasses (30 ≤ x ≤ 60) were fabricated by the aerodynamic levitation technique. The elastic moduli and Vickers hardness monotonically increased with an increase in the atomic packing density as the Al2O3 content increased. Although a higher atomic packing density generally enhances crack formation in conventional oxide glasses, the indentation cracking resistance increased by approximately seven times with an increase in atomic packing density in binary Al2O3-SiO2 glasses. In particular, the composition of 60Al2O3 • 40SiO2 glass, which is identical to that of mullite, has extraordinary high cracking resistance with high elastic moduli and Vickers hardness. The results indicate that there exist aluminosilicate compositions that can produce hard and damage-tolerant glasses.

| S-EPMC4823710 | biostudies-other

The Critical Criterion on Runaway Shear Banding in Metallic Glasses.

Project description:The plastic flow of metallic glasses (MGs) in bulk is mediated by nanoscale shear bands, which is known to proceed in a stick-slip manner until reaching a transition state causing catastrophic failures. Such a slip-to-failure transition controls the plasticity of MGs and resembles many important phenomena in natural science and engineering, such as friction, lubrication and earthquake, therefore has attracted tremendous research interest over past decades. However, despite the fundamental and practical importance, the physical origin of this slip-to-failure transition is still poorly understood. By tracking the behavior of a single shear band, here we discover that the final fracture of various MGs during compression is triggered as the velocity of the dominant shear band rises to a critical value, the magnitude of which is independent of alloy composition, sample size, strain rate and testing frame stiffness. The critical shear band velocity is rationalized with the continuum theory of liquid instability, physically originating from a shear-induced cavitation process inside the shear band. Our current finding sheds a quantitative insight into deformation and fracture in disordered solids and, more importantly, is useful to the design of plastic/tough MG-based materials and structures.

| S-EPMC4759565 | biostudies-literature

Indentation Response of Calcium Aluminoborosilicate Glasses Subjected to Humid Aging and Hot Compression.

Project description:Aluminoborosilicate glasses find a wide range of applications, which require good mechanical reliability such as surface damage resistance. Calcium aluminoborosilicate (CABS) glasses have recently been found to exhibit so-called intermediate behavior in terms of their response to sharp contact loading. That is, these glasses deform with less shear than normal glass and less densification than anomalous glasses. This deformation mechanism is believed to give rise to high crack initiation resistance of certain CABS glasses. In order to further improve and understand the micromechanical properties of this glass family, we studied the indentation response of different CABS glasses subjected to two types of post-treatment, namely hot compression and humid aging. Upon hot compression, density, elastic moduli, and hardness increased. Specifically, elastic modulus increased by as much as 20% relative to the as-made sample, while the largest change in hardness was 1.8 GPa compared to the as-made sample after hot compression. The pressure-induced increase in these properties can be ascribed to the increase in network connectivity and bond density. On the other hand, the crack initiation resistance decreased, as the hot compression increased the residual stress driving the indentation cracking. Humid aging had only a minor impact on density, modulus, and hardness, but an observed decrease in crack initiation resistance. We discuss the correlations between hardness, density, crack resistance, and deformation mechanism and our study thus provides guidelines for tailoring the mechanical properties of oxide glasses.

| S-EPMC8269477 | biostudies-literature

Fretting Fatigue with Cylindrical-On-Flat Contact: Crack Nucleation, Crack Path and Fatigue Life.

Project description:Fretting fatigue experiments and finite element analysis were carried out to investigate the influence of cylindrical-on-flat contact on crack nucleation, crack path and fatigue life of medium-carbon steel. The location of crack nucleation was predicted using the maximum shear stress range criterion and the maximum relative slip amplitude criterion. The prediction using the maximum relative slip amplitude criterion gave the better agreement with the experimental result, and should be used for the prediction of the location of crack nucleation. Crack openings under compressive bulk stresses were found in the fretting fatigues with flat-on-flat contact and cylindrical-on-flat contacts, i.e., fretting-contact-induced crack openings. The crack opening stress of specimen with flat-on-flat contact was lower than those of specimens with cylindrical-on-flat contacts, while that of specimen with 60-mm radius contact pad was lower than that of specimen with 15-mm radius contact pad. The fretting fatigue lives were estimated by integrating the fatigue crack growth curve from an initial propagating crack length to a critical crack length. The predictions of fretting fatigue life with consideration of crack opening were in good agreement with the experimental results.

| S-EPMC5459140 | biostudies-other

Compositional Effects on Indentation Mechanical Properties of Chemically Strengthened TiO2-Doped Soda Lime Silicate Glasses.

Project description:TiO2 is an important oxide for property modifications in the conventional soda lime silicate glass family. It offers interesting optical and mechanical properties, for instance, by substituting heavy metals such as lead in consumer glasses. The compositional effects on the hardness, reduced elastic modulus and crack resistance as determined by indentation of chemically strengthened (CS) TiO2-doped soda lime silicate glass was studied in the current paper. The CS, which was performed by a K+ for Na+ ion exchange in a molten KNO3 salt bath at 450 °C for 15 h, yielded significant changes in the indentation mechanical properties. The hardness of the glass samples increased, and this was notably dependent on the SiO2, CaO and TiO2 content. The reduced elastic modulus was less affected by the CS but showed decrease for most samples. The crack resistance, an important property in many applications where glasses are subjected to contact damage, showed very different behaviors among the series. Only one of the series did significantly improve the crack resistance where low CaO content, high TiO2 content, high molar volume and increased elastic deformation favored an increased crack resistance.

| S-EPMC8779215 | biostudies-literature

Quantification of dislocation nucleation stress in TiN through high-resolution in situ indentation experiments and first principles calculations.

Project description:Through in situ indentation of TiN in a high-resolution transmission electron microscope, the nucleation of full as well as partial dislocations has been observed from {001} and {111} surfaces, respectively. The critical elastic strains associated with the nucleation of the dislocations were analyzed from the recorded atomic displacements, and the nucleation stresses corresponding to the measured critical strains were computed using density functional theory. The resolved shear stress was estimated to be 13.8 GPa for the partial dislocation 1/6 <110> {111} and 6.7 GPa for the full dislocation ½ <110> {110}. Such an approach of quantifying nucleation stresses for defects via in situ high-resolution experiment coupled with density functional theory calculation may be applied to other unit processes.

| S-EPMC4633591 | biostudies-literature

Predictive modeling of Time-Temperature-Transformation diagram of metallic glasses based on atomistically-informed classical nucleation theory.

Project description:Theoretical prediction of glass forming ability (GFA) of metallic alloys is a key process in exploring metallic alloy compositions with excellent GFA and thus with the ability to form a large-sized bulk metallic glass. Molecular dynamics (MD) simulation is a promising tool to achieve a theoretical prediction. However, direct MD prediction continues to be challenging due to the time-scale limitation of MD. With respect to practical bulk metallic glass alloys, the time necessary for quenching at a typical cooling rate is five or more orders of magnitude higher than that at the MD time-scale. To overcome the time-scale issue, this study proposes a combined method of classical nucleation theory and MD simulations. The method actually allows to depict the time-temperature-transformation (TTT) diagram of the bulk metallic glass alloys. The TTT directly provides a prediction of the critical cooling rate and GFA. Although the method assumes conventional classical nucleation theory, all the material parameters appearing in the theory were determined by MD simulations using realistic interatomic potentials. The method is used to compute the TTT diagrams and critical cooling rates of two Cu-Zr alloy compositions (Cu50Zr50 and Cu20Zr80). The results indicate that the proposed method reasonably predicts the critical cooling rate based on the computed TTT.

| S-EPMC5543070 | biostudies-literature

Low-temperature nucleation anomaly in silicate glasses shown to be artifact in a 5BaO·8SiO<sub>2</sub> glass.

Project description:For over 40 years, measurements of the nucleation rates in a large number of silicate glasses have indicated a breakdown in the Classical Nucleation Theory at temperatures below that of the peak nucleation rate. The data show that instead of steadily decreasing with decreasing temperature, the work of critical cluster formation enters a plateau and even starts to increase. Many explanations have been offered to explain this anomaly, but none have provided a satisfactory answer. We present an experimental approach to demonstrate explicitly for the example of a 5BaO ∙ 8SiO2 glass that the anomaly is not a real phenomenon, but instead an artifact arising from an insufficient heating time at low temperatures. Heating times much longer than previously used at a temperature 50 K below the peak nucleation rate temperature give results that are consistent with the predictions of the Classical Nucleation Theory. These results raise the question of whether the claimed anomaly is also an artifact in other glasses.

| S-EPMC8016887 | biostudies-literature

Beyond Rayleigh's criterion: a resolution measure with application to single-molecule microscopy.

Project description:Rayleigh's criterion is extensively used in optical microscopy for determining the resolution of microscopes. This criterion imposes a resolution limit that has long been held as an impediment for studying nanoscale biological phenomenon through an optical microscope. However, it is well known that Rayleigh's criterion is based on intuitive notions. For example, Rayleigh's criterion is formulated in a deterministic setting that neglects the photon statistics of the acquired data. Hence it does not take into account the number of detected photons, which, in turn, raises concern over the use of Rayleigh's criterion in photon-counting techniques such as single-molecule microscopy. Here, we re-examine the resolution problem by adopting a stochastic framework and present a resolution measure that overcomes the limitations of Rayleigh's criterion. This resolution measure predicts that the resolution of optical microscopes is not limited and that it can be improved by increasing the number of detected photons. Experimental verification of the resolution measure is carried out by imaging single-molecule pairs with different distances of separation. The resolution measure provides a quantitative tool for designing and evaluating single-molecule experiments that probe biomolecular interactions.

| S-EPMC1450193 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data