Two Independent Prospectively Planned Blinded Weibull Statistical Analyses of Flexural Strength Data of Zirconia Materials.
Ontology highlight
ABSTRACT:
SUBMITTER: Roos M
PROVIDER: S-EPMC5456914 | biostudies-other | 2016 Jun
REPOSITORIES: biostudies-other
Similar Datasets
Project description:One therapeutical alternative in the treatment of functional disorders is the use of printed oral splints. The mechanical properties of these materials are highly essential to their clinical effectiveness, and their performance may vary depending on factors such as cleaning, post-polymerization, or their orientation during construction. The objective of this in vitro investigation is to evaluate the effectiveness of the selected materials in terms of their biaxial flexural strength in relation to the criteria listed above. Splint materials were used in the printing of 720 discs. The printing process was carried out in different orientations in relation to the building platform. Either an automatic or manual cleaning process was performed on the samples. For post-polymerization, either an LED or Xenon light was utilized. A piston-on-three-ball test was used to measure the biaxial flexural strength (BFS) of the materials after they were stored in water for either 24 h or 60 days. The homogeneity of the data was controlled by employing the Levene method, and the differences between the groups were analyzed using the ANOVA and Bonferroni methods. After being stored for twenty-four hours, the mean BFS ranged anywhere from 79 MPa to 157 MPa. Following a period of sixty hours, the BFS exhibited a substantial drop and revealed values that ranged from 72 to 127 MPa. There was no significant difference that could be identified between the materials or between the various cleaning processes. The results of post-polymerization showed that the LED light produced higher means than the Xenon light did. In terms of position, the mean values varied greatly, with 0°'s mean value being 101 MPa, 45°'s mean value being 102 MPa, and 90°'s mean value being 115 MPa. The use of a build orientation of 90° and post-polymerization with LED light resulted in significantly increased biaxial flexural strength. According to this study, this design should be implemented in order to ensure that splint materials have the highest possible strength.
| S-EPMC10934272 | biostudies-literature
Project description:The aim of this work was to evaluate the influence of specimen preparation and test method on the flexural strength results of monolithic zirconia. Different monolithic zirconia materials (Ceramill Zolid (Amann Girrbach, Koblach, Austria), Zenostar ZrTranslucent (Wieland Dental, Pforzheim, Germany), and DD Bio zx² (Dental Direkt, Spenge, Germany)) were tested with three different methods: 3-point, 4-point, and biaxial flexural strength. Additionally, different specimen preparation methods were applied: either dry polishing before sintering or wet polishing after sintering. Each subgroup included 40 specimens. The surface roughness was assessed using scanning electron microscopy (SEM) and a profilometer whereas monoclinic phase transformation was investigated with X-ray diffraction. The data were analyzed using a three-way Analysis of Variance (ANOVA) with respect to the three factors: zirconia, specimen preparation, and test method. One-way ANOVA was conducted for the test method and zirconia factors within the combination of two other factors. A 2-parameter Weibull distribution assumption was applied to analyze the reliability under different testing conditions. In general, values measured using the 4-point test method presented the lowest flexural strength values. The flexural strength findings can be grouped in the following order: 4-point < 3-point < biaxial. Specimens prepared after sintering showed significantly higher flexural strength values than prepared before sintering. The Weibull moduli ranged from 5.1 to 16.5. Specimens polished before sintering showed higher surface roughness values than specimens polished after sintering. In contrast, no strong impact of the polishing procedures on the monoclinic surface layer was observed. No impact of zirconia material on flexural strength was found. The test method and the preparation method significantly influenced the flexural strength values.
| S-EPMC5456702 | biostudies-other
Project description:The clinical application of 3D-printed provisional restorations is increasing due to expansion of intraoral scanners, easy dental computer-aided design (CAD) software, and improved 3D printing speed. This study compared flexural strength of 3D-printed three-unit fixed dental prostheses with that of conventionally fabricated and milled restorations. A metal jig of two abutments and pontic space and an indenter for flexural strength measurement were fabricated. A three-unit fixed dental prosthesis was designed and manufactured using three additive manufacturing technologies, with subtractive manufacturing and a conventional method as controls. Digital light processing (DLP) group specimens were prepared from a polymethyl methacrylate (PMMA)-based resin and printed with a DLP printer. Stereolithography (SLA) group specimens were prepared from PMMA-based resin and printed with an SLA printer, and fused deposition modeling (FDM) group specimens were from a polylactic acid-based resin and printed with an FDM printer. Flexural strength was investigated using a universal testing machine, and the results were statistically analyzed. DLP and SLA groups had significantly higher flexural strength than the conventional group (p < 0.001). No significant difference was observed in flexural strength between DLP and SLA groups. The FDM group showed only dents but no fracture. The results of this study suggest that provisional restorations fabricated by DLP and SLA technologies provide adequate flexural strength for dental use.
| S-EPMC7559938 | biostudies-literature
Project description:The aim of this work was to evaluate the effects of application time of an acid mixture solution on the surface roughness, phase transformation, and biaxial flexural strength of 3Y-TZP after sintering or air abrasion. For the biaxial flexural strength measurement, 220 3Y-TZP disk-shaped specimens were prepared after as-sintering or air abrasion. The etching solution comprised a mixture of hydrofluoric acid, sulfuric acid, hydrogen peroxide, methyl alcohol, and purified water. The samples were divided into 11 subgroups according to the etching times (Control, 1, 2, 3, 5, 8, 10, 12, 15, 20, and 30 min). The results showed that acid treatment on both as-sintered and air-abraded 3Y-TZP surfaces increased the surface roughness. However, it had no significant effects on the monoclinic phase or flexural strength of as-sintered zirconia. The monoclinic phase and flexural strength of air-abraded zirconia increased sharply after air abrasion; however, they gradually decreased after acid treatment, to a similar level to the case of the untreated surface. Surface treatment with acid mixture increased the roughness, but the lack of increase of monoclinic phase is thought to be because the loose monoclinic particles remaining on the surface were removed through the etching process.
| S-EPMC8125152 | biostudies-literature
Project description:BACKGROUND:Choosing or altering the planned statistical analysis approach after examination of trial data (often referred to as 'p-hacking') can bias the results of randomised trials. However, the extent of this issue in practice is currently unclear. We conducted a review of published randomised trials to evaluate how often a pre-specified analysis approach is publicly available, and how often the planned analysis is changed. METHODS:A review of randomised trials published between January and April 2018 in six leading general medical journals. For each trial, we established whether a pre-specified analysis approach was publicly available in a protocol or statistical analysis plan and compared this to the trial publication. RESULTS:Overall, 89 of 101 eligible trials (88%) had a publicly available pre-specified analysis approach. Only 22/89 trials (25%) had no unexplained discrepancies between the pre-specified and conducted analysis. Fifty-four trials (61%) had one or more unexplained discrepancies, and in 13 trials (15%), it was impossible to ascertain whether any unexplained discrepancies occurred due to incomplete reporting of the statistical methods. Unexplained discrepancies were most common for the analysis model (n?=?31, 35%) and analysis population (n?=?28, 31%), followed by the use of covariates (n?=?23, 26%) and the approach for handling missing data (n?=?16, 18%). Many protocols or statistical analysis plans were dated after the trial had begun, so earlier discrepancies may have been missed. CONCLUSIONS:Unexplained discrepancies in the statistical methods of randomised trials are common. Increased transparency is required for proper evaluation of results.
| S-EPMC7257229 | biostudies-literature
Project description:Soil?cement is an environmentally friendly road construction technique for base and subbase materials, which allows employing soils placed in the right-of-way of the road or in the surroundings, by improving its engineering properties. With this technique, it is possible to reduce the over-exploitation of quarries, the necessity of landfills and the pollutant gas emission due to the reduction of aggregate fabrication and transport. The manufacturing of soil?cement is generally controlled by means of the Uniaxial Compressive Strength (UCS) test at seven days, according to the regulations of each country. Nonetheless, one of the properties that best defines the performance of soil?cement is the Flexural Strength (FS) at long term, usually at 90 days. The aim of this paper is to develop new equations to correlate the UCS and the FS at long term and the UCS at seven days and at 90 days. Obtained results validate the proposed models and, hence, the flexural strength can be predicted from the Uniaxial Compressive Strength at seven days, allowing, if necessary, correcting measures (recalculation or rejection) in early stages of the curing time to be taken.
| S-EPMC6384646 | biostudies-literature
Project description:This study evaluated the shear bond strength (SBS) and biaxial flexural strength (BFS) of resin cements according to the surface treatment method using low-temperature hot etching with hydrofluoric acid (HF) on a yttrium-stabilized tetragonal zirconia (Y-TZP) surface; 96 discs and 72 cubes for BFS and SBS tests for Y-TZP were randomly divided into four groups of BFS and three groups of SBS. Specimens were subjected to the following surface treatments: (1) no treatment (C), (2) air abrasion with 50 ?m Al2O3 particles (A), (3) hot etching with HF at 100 °C for 10 min (E), and (4) air abrasion + hot etching (AE). After treatments, the specimens were coated with primer, and resin cement was applied with molds. The specimens were evaluated for roughness (Ra) via scanning electron microscopy and x-ray diffraction, and the data were analyzed by an analysis of variance (ANOVA) and Kruskal-Wallis tests. Group E produced significantly higher SBS compared to group A and AE before and after thermocycling. The BFSs of all groups showed no significant differences before thermocycling; however, after thermocycling, C and E treatment groups were significantly higher compared to group A and AE. All groups showed phase transformation. Group E was observed lower monoclinic phase transformation compared to other groups.
| S-EPMC7143885 | biostudies-literature
Project description:Esthetic dental computer-aided design/computer-aided manufacturing (CAD/CAM) polymers such as disperse-filled composites (DFC) and polymer-infiltrated ceramic networks (PICN) should be subjected to surface treatment before bonding. However, such treatment can lead to defect formation and a decrease in strength. Therefore, in this study, we compared the flexural strengths of DFC and PICN materials air-abraded with alumina particles of different sizes at different pressures. In addition to Weibull analysis, the samples (untreated and treated) were characterized by scanning electron microscopy and atomic force microscopy. Both DFC and PICN exhibited the lowest flexural strength at large particle sizes and high pressures. Therefore, we optimized the air abrasion parameters to maintain the flexural strength and significantly increase surface roughness. In the case of DFC, the optimal particle size and pressure conditions were 50 µm at 2 bar and 110 µm at 1 bar, while for PICN, the best performance was obtained using Al2O3 particles with a size of 50 µm at 1 bar. This study reveals that optimization of the surface treatment process is crucial in the fabrication of high-performance clinical materials for dental restorations.
| S-EPMC7362000 | biostudies-literature
Project description:Interictal high-frequency oscillations are discussed as biomarkers for epileptogenic brain tissue that should be resected in epilepsy surgery to achieve seizure freedom. The prospective classification of tissue sampled by individual electrode contacts remains a challenge. We have developed an automated, prospective definition of clinically relevant high-frequency oscillations in intracranial EEG from Montreal and tested it in recordings from Zurich. We here validated the algorithm on intracranial EEG that was recorded in an independent epilepsy centre so that the analysis was blinded to seizure outcome. We selected consecutive patients who underwent resective epilepsy surgery in Geneva with post-surgical follow-up > 12 months. We analysed long-term recordings during sleep that we segmented into intervals of 5 min. High-frequency oscillations were defined in the ripple (80-250 Hz) and the fast ripple (250-500 Hz) frequency bands. Contacts with the highest rate of ripples co-occurring with fast ripples designated the relevant area. As a validity criterion, we calculated the test-retest reliability of the high-frequency oscillations area between the 5 min intervals (dwell time ≥50%). If the area was not fully resected and the patient suffered from recurrent seizures, this was classified as a true positive prediction. We included recordings from 16 patients (median age 32 years, range 18-53 years) with stereotactic depth electrodes and/or with subdural electrode grids (median follow-up 27 months, range 12-55 months). For each patient, we included several 5 min intervals (median 17 intervals). The relevant area had high test-retest reliability across intervals (median dwell time 95%). In two patients, the test-retest reliability was too low (dwell time < 50%) so that outcome prediction was not possible. The area was fully included in the resected volume in 2/4 patients who achieved post-operative seizure freedom (specificity 50%) and was not fully included in 9/10 patients with recurrent seizures (sensitivity 90%), leading to an accuracy of 79%. An additional exploratory analysis suggested that high-frequency oscillations were associated with interictal epileptic discharges only in channels within the relevant area and not associated in channels outside the area. We thereby validated the automated procedure to delineate the clinically relevant area in each individual patient of an independently recorded dataset and achieved the same good accuracy as in our previous studies. The reproducibility of our results across datasets is promising for a multicentre study to test the clinical application of high-frequency oscillations to guide epilepsy surgery.
| S-EPMC8445392 | biostudies-literature
Project description:The additive manufacturing of concrete, also known as 3D-printed concrete, is produced layer by layer using a 3D printer. The three-dimensional printing of concrete offers several benefits compared to conventional concrete construction, such as reduced labor costs and wastage of materials. It can also be used to build complex structures with high precision and accuracy. However, optimizing the mix design of 3D-printed concrete is challenging, involving numerous factors and extensive hit-and-trail experimentation. This study addresses this issue by developing predictive models, such as the Gaussian Process Regression model, Decision Tree Regression model, Support Vector Machine model, and XGBoost Regression models. The input parameters were water (Kg/m3), cement (Kg/m3), silica fume (Kg/m3), fly ash (Kg/m3), coarse aggregate (Kg/m3 & mm for diameter), fine aggregate (Kg/m3 & mm for diameter), viscosity modifying agent (Kg/m3), fibers (Kg/m3), fiber properties (mm for diameter and MPa for strength), print speed (mm/sec), and nozzle area (mm2), while target properties were the flexural and tensile strength of concrete (MPa data from 25 literature studies were collected. The water/binder ratio used in the dataset ranged from 0.27 to 0.67. Different types of sands and fibers have been used, with fibers having a maximum length of 23 mm. Based upon the Coefficient of Determination (R2), Root Mean Square Error (RMSE), Mean Square Error (MSE), and Mean Absolute Error (MAE) for casted and printed concrete, the SVM model performed better than other models. All models' cast and printed flexural strength values were also correlated. The model's performance has also been checked on six different mix proportions from the dataset to show its accuracy. It is worth noting that the lack of ML-based predictive models for the flexural and tensile properties of 3D-printed concrete in the literature makes this study a novel innovation in the field. This model could reduce the computational and experimental effort required to formulate the mixed design of printed concrete.
| S-EPMC10254869 | biostudies-literature