Repair Bond Strength of Aged Resin Composite after Different Surface and Bonding Treatments.

ABSTRACT: The aim of this study was to compare the effect of different mechanical surface treatments and chemical bonding protocols on the tensile bond strength (TBS) of aged composite. Bar specimens were produced using a nanohybrid resin composite and aged in distilled water for 30 days. Different surface treatments (diamond bur, phosphoric acid, silane, and sandblasting with Al₂O₃ or CoJet Sand), as well as bonding protocols (Primer/Adhesive) were used prior to application of the repair composite. TBS of the specimens was measured and the results were analyzed using analysis of variance (ANOVA) and the Student-Newman-Keuls test (α = 0.05). Mechanically treated surfaces were characterized under SEM and by profilometry. The effect of water aging on the degree of conversion was measured by means of FTIR-ATR spectroscopy. An important increase in the degree of conversion was observed after aging. No significant differences in TBS were observed among the mechanical surface treatments, despite variations in surface roughness profiles. Phosphoric acid etching significantly improved repair bond strength values. The cohesive TBS of the material was only reached using resin bonding agents. Application of an intermediate bonding system plays a key role in achieving reliable repair bond strengths, whereas the kind of mechanical surface treatment appears to play a secondary role.

SUBMITTER: Wendler M

PROVIDER: S-EPMC5456933 | biostudies-other | 2016 Jul

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Effect of Different Surface Treatments on the Long-Term Repair Bond Strength of Aged Methacrylate-Based Resin Composite Restorations: A Systematic Review and Network Meta-analysis

Project description: Not available

| S-EPMC10643039 | biostudies-literature

Effect of Various Laser Surface Treatments on Repair Shear Bond Strength of Aged Silorane-Based Composite.

Project description:Introduction: Successful repair of composite restorations depends on a strong bond between the old composite and the repair composite. This study sought to assess the repair shear bond strength of aged silorane-based composite following surface treatment with Nd:YAG, Er,Cr:YSGG and CO2 lasers. Methods: Seventy-six Filtek silorane composite cylinders were fabricated and aged by 2 months of water storage at 37°C. The samples were randomly divided into 4 groups (n=19) of no surface treatment (group 1) and surface treatment with Er,Cr:YSGG (group 2), Nd:YAG (group 3) and CO2 (group 4) lasers. The repair composite was applied and the shear bond strength was measured. The data were analyzed using one-way analysis of variance (ANOVA) and Tukey posthoc test. Prior to the application of the repair composite, 2 samples were randomly selected from each group and topographic changes on their surfaces following laser irradiation were studied using a scanning electron microscope (SEM). Seventeen other samples were also fabricated for assessment of cohesive strength of composite. Results: The highest and the lowest mean bond strength values were 8.99 MPa and 6.69 MPa for Er,Cr:YSGG and control groups, respectively. The difference in the repair bond strength was statistically significant between the Er,Cr:YSGG and other groups. Bond strength of the control, Nd:YAG and CO2 groups was not significantly different. The SEM micrographs revealed variable degrees of ablation and surface roughness in laser-treated groups. Conclusion: Surface treatment with Er,Cr:YSGG laser significantly increase the repair bond strength of aged silorane-based composite resin.

| S-EPMC5642167 | biostudies-other

Effect of different surface treatments on the shear bond strength of nanofilled composite repairs.

Project description:Background. Repairing aged composite resin is a challenging process. Many surface treatment options have been proposed to this end. This study evaluated the effect of different surface treatments on the shear bond strength (SBS) of nano-filled composite resin repairs. Methods. Seventy-five cylindrical specimens of a Filtek Z350XT composite resin were fabricated and stored in 37°C distilled water for 24 hours. After thermocycling, the specimens were divided into 5 groups according to the following surface treatments: no treatment (group 1); air abrasion with 50-μm aluminum oxide particles (group 2); irradiation with Er:YAG laser beams (group 3); roughening with coarse-grit diamond bur + 35% phosphoric acid (group 4); and etching with 9% hydrofluoric acid for 120 s (group 5). Another group of Filtek Z350XT composite resin samples (4×6 mm) was fabricated for the measurement of cohesive strength (group 6). A silane coupling agent and an adhesive system were applied after each surface treatment. The specimens were restored with the same composite resin and thermocycled again. A shearing force was applied to the interface in a universal testing machine. Data were analyzed using one-way ANOVA and post hoc Tukey tests (P < 0.05). Results. One-way ANOVA indicated significant differences between the groups (P < 0.05). SBS of controls was significantly lower than the other groups; differences between groups 2, 3, 4, 5 and 6 were not significant. Surface treatment with diamond bur + 35% phosphoric acid resulted in the highest bond strength. Conclusion. All the surface treatments used in this study improved the shear bond strength of nanofilled composite resin used.

| S-EPMC4831615 | biostudies-other

Shear Bond Strength of Self-Adhesive Flowable Resin Composite.

Project description:This study aimed to evaluate the shear bond strength of self-adhesive flowable resin composite on both enamel and dentin and investigate whether surface pretreatment with a phosphoric acid etch affects the bond strength. In this in vitro study, 80 sound human premolars were flattened to create (40) uniform enamel (E) and (40) dentin (D) surfaces. Groups were divided according to surface pretreatment: E1 : Scotchbond™ Universal Etchant + Single Bond Universal Adhesive + Filtek™ Z350 XT flowable composite; E2: Single Bond Universal self-etch adhesive + Filtek Z350 XT flowable composite; E3 : Scotchbond Universal Etchant + Fusio Liquid Dentin self-adhesive flowable composite; E4: Fusio Liquid Dentin self-adhesive flowable composite; D1 : Scotchbond Universal Etchant + Single Bond Universal Adhesive + Filtek Z350 XT flowable composite; D2: Single Bond Universal self-etch adhesive + Filtek Z350 XT flowable composite; D3: Scotchbond Universal Etchant + Fusio Liquid Dentin self-adhesive flowable composite; D4: Fusio Liquid Dentin self-adhesive flowable composite. After 2500 thermal cycles, the SBS was measured with a universal testing machine. One-way analysis of variance and Tukey's test for multiple comparisons were used to compare results. Two-way ANOVA was done to observe the significance of interaction between the type of surface and treatment. The maximum (49.38 ± 1.23 MPa) and minimum (21.41 ± 5.27 MPa) SBS values were noted in groups D1 and E2, respectively. Shear bond test results showed that self-adhesive flowable composite exhibited similar shear bond strengths on enamel and dentin and the bond strength improved with selective acid etching.

| S-EPMC9106484 | biostudies-literature

Effects of cyclic loading on the shear bond strength of metal orthodontic brackets bonded to resin composite veneer surface using different conditioning protocols.

Project description:The aim of this research is to evaluate cyclic (CSBS) and static shear bond strengths (SSBS) of metal orthodontic brackets bonded to composite laminates using different conditioning protocols.A total of 80 direct nanofilled composite laminate veneers were prepared on permanent incisors and divided into four equal groups according to different surface treatments. In group 1, diamond bur was used. In group 2, microetcher (50-?m alumina particles) was utilized. In group 3, 38% phosphoric acid treatment for 60 s was done. In group 4 (control group), metal brackets were bonded to the untreated veneer surfaces using no-mix adhesive resin. SSBS testing was carried out for ten specimens, while CSBS testing was done for another ten specimens from each group. The data were subjected to analysis of variance and Scheffe post hoc test. The chi-square test was used to determine significant differences in the adhesive remnant index scores among different groups.Statistically significant difference was only found between SSBS of brackets bonded when surface treatment was done using the diamond bur, microetcher, and the phosphoric acid at P<0.05. With regard to CSBS, the use of bur treatment and microetching achieved the highest values; however, there was no significant difference between these two groups. With phosphoric acid, surface treatment achieved the lowest CSBS value; there was no significant difference between this group and the control group. The SSBS was significantly higher than CSBS in all groups.Roughening composite laminate veneers with either diamond bur or microetcher could be used successfully as an alternative to provide higher bond strength than phosphoric acid surface treatment. Cyclic loading significantly decreased bond strength.

| S-EPMC4406983 | biostudies-literature

Micro-shear bond strength of different surface treatments on a polymer infiltrated ceramic network.

Project description:Background: Polymer infiltrated ceramic networks, or hybrid ceramics, are a combination of infiltrating polymerizable organic monomers into a pre-sintered porous ceramic matrix. In addition to having good mechanical properties, the polymer infiltrated ceramic network must comply with the possibility of adequate bonding to the resinous cement. The surface conditioning of this hybrid material must be carefully considered due to its organic composition and ceramic network. The purpose of this research is to evaluate the effect of hydrofluoric acid and a self-etching ceramic primer, under two different application times, on the bond strength of a polymer infiltrated ceramic network. Methods: Blocks of a polymer infiltrated ceramic network were cut to obtain sheets, and these were randomized into five groups. For the group termed AAS, airborne-particle abrasion with Al 2O 3 (aluminum oxide) of 50µm was used. For groups HF2 and HF6, hydrofluoric acid was used for 20 and 60 seconds respectively, and for the groups MB2 and MB6, a self-etch ceramic primer was applied for 20 and 60 seconds respectively. A silane was applied to the groups AAS, HF2, and HF6 after the treatment. After 24-hour storage in distilled water, a micro-shear bond strength test was performed using a universal mechanical testing machine. All samples were evaluated in a stereomicroscope at 40x and 50x to determine the type of failure. Results: The highest and lowest values of bond strength were reported by groups MB6 and AAS, respectively. Groups HF2, HF6, MB6, and MB2 did not report statistically significant differences. The predominant failure pattern was a mixed failure. Conclusions: With the limitations of the present investigation, the treatments of self-etching ceramic primer and hydrofluoric acid followed by silane were reported to be statistically equal at 20 and 60 seconds.

| S-EPMC10665602 | biostudies-literature

Comparative Evaluation of the Repair Bond Strength of Dental Resin Composite after Sodium Bicarbonate or Aluminum Oxide Air-Abrasion.

Project description:The dental prophylactic cleaning of a damaged resin-based composite (RBC) restoration with sodium bicarbonate can change the surface characteristics and influence the repair bond strength. The purpose of this study was to compare the effect of sodium bicarbonate (SB) and aluminum oxide (AO) surface treatments on the microtensile bond strength (µTBS) of repaired, aged RBC. Bar specimens were prepared from microhybrid RBC and aged in deionized water for 8 weeks. Different surface treatments (AO air-abrasion; SB air-polishing), as well as cleaning (phosphoric acid, PA; ethylene-diamine-tetraacetic-acid, EDTA) and adhesive applications (single bottle etch-and-rinse, ER; universal adhesive, UA), were used prior to the application of the repair RBC. Not aged and aged but not surface treated RBCs were used as positive and negative controls, respectively. The repaired blocks were cut into sticks using a precision grinding machine. The specimens were tested for tensile fracture and the µTBS values were calculated. Surface characteristics were assessed using scanning electron microscopy. AO-PA-UA (62.6 MPa) showed a 20% increase in µTBS compared to the NC (50.2 MPa), which proved to be the most significant. This was followed by SB-EDTA-UA (58.9 MPa) with an increase of 15%. In addition to AO-PA-UA, SB-EDTA-UA could also be a viable alternative in the RBC repair protocol.

| S-EPMC10380324 | biostudies-literature

Influence of Different Surface Pretreatments on Shear Bond Strength of an Adhesive Resin Cement to Various Zirconia Ceramics.

Project description:The aim of this in vitro study was to assess the influence of surface pretreatment on shear bond strength (SBS) of an adhesive resin cement (G-CEM Link Force TM, GC Corporation, Tokyo, Japan) to three different yttria-stabilized tetragonal zirconia polycrystalline (Y-TZP) ceramics: (1) Copran Zirconia Monolith HT, COP; (2) Katana ML Zirconia, KAT; and (3) Metoxit Z-CAD HTL Zirconia, MET. In total, 45 cylinders (5 mm in diameter, 1 mm height) for each type of zirconia ceramic were prepared used a computer-aided design and computer-aided manufacturing (CAD/CAM) machine (software CEREC 4.2). Each type of zirconia was subdivided into three groups and each group received a different surface pretreatment; 15 samples were not conditioned as control (groups COP 1, KAT 1, MET 1), 15 samples were air-borne particle abraded with aluminum dioxide particles of 50-?m size at 0.3 MPa for 20 s (groups COP 2, KAT 2, MET 2), and 15 samples were hot-etched with a solution of hydrochloric acid and ferric chloride (groups COP 3, KAT 3, MET 3). After specimen fabrication, the adhesive cement-ceramic interface was analyzed using an SBS test. Subsequently, the adhesive remnant index (ARI) was measured. Data were submitted to statistical analysis. Air-borne particle abraded specimens showed the highest SBS values for COP and KAT groups. For MET, no significant difference was reported between air-borne particle abraded specimens and untreated controls. The lowest values were detected for acid-etched groups. A higher frequency of ARI = "1" and ARI = "2" was reported in control and air-borne particle abraded groups, whereas ARI = "3" was detected in hot-etched groups. No correlation was found between ARI score and shear bond strength. Air-borne particle abrasion is considered the best treatment for Zirconia Copran and Zirconia Katana ML, if it is followed by using dual-curing resin cement.

| S-EPMC7040603 | biostudies-literature

Influence of Hot-Etching Surface Treatment on Zirconia/Resin Shear Bond Strength.

Project description:This study was designed to evaluate the effect of hot-etching surface treatment on the shear bond strength between zirconia ceramics and two commercial resin cements. Ceramic cylinders (120 units; length: 2.5 mm; diameter: 4.7 mm) were randomly divided into 12 groups (n = 10) according to different surface treatments (blank control; airborne-particle-abrasion; hot-etching) and different resin cements (Panavia F2.0; Superbond C and B) and whether or not a thermal cycling fatigue test (5°-55° for 5000 cycles) was performed. Flat enamel surfaces, mounted in acrylic resin, were bonded to the zirconia discs (diameter: 4.7 mm). All specimens were subjected to shear bond strength testing using a universal testing machine with a crosshead speed of 1 mm/min. All data were statistically analyzed using one-way analysis of variance and multiple-comparison least significant difference tests (α = 0.05). Hot-etching treatment produced higher bond strengths than the other treatment with both resin cements. The shear bond strength of all groups significantly decreased after the thermal cycling test; except for the hot-etching group that was cemented with Panavia F2.0 (p < 0.05). Surface treatment of zirconia with hot-etching solution enhanced the surface roughness and bond strength between the zirconia and the resin cement.

| S-EPMC5458836 | biostudies-other

Influence of Pre-Sintered Zirconia Surface Conditioning on Shear Bond Strength to Resin Cement.

Project description:This study analyzed the shear bond strength (SBS) of resin composite on zirconia surface to which a specific conditioner was applied before sintering. After sintering of either conditioner-coated or uncoated specimens, both groups were divided into three subgroups by their respective surface modifications (n = 10 per group): no further treatment; etched with hydrofluoric acid; and sandblasted with 50 µm Al₂O₃ particles. Surfaces were characterized by measuring different surface roughness parameters (e.g., Ra and Rmax) and water contact angles. Half of the specimens underwent thermocycling (10,000 cycles, 5-55 °C) after self-adhesive resin cement build-up. The SBSs were measured using a universal testing machine, and the failure modes were analyzed by microscopy. Data were analyzed by nonparametric and parametric tests followed by post-hoc comparisons (α = 0.05). Conditioner-coated specimens increased both surface roughness and hydrophilicity (p < 0.01). In the non-thermocycled condition, sandblasted surfaces showed higher SBSs than other modifications, irrespective of conditioner application (p < 0.05). Adhesive fractures were commonly observed in the specimens. Thermocycling favored debonding and decreased SBSs. However, conditioner-coated specimens upon sandblasting showed the highest SBS (p < 0.05) and mixed fractures were partially observed. The combination of conditioner application before sintering and sandblasting after sintering showed the highest shear bond strength and indicated improvements concerning the failure mode.

| S-EPMC5456913 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data