Current Insights into the Modulation of Oral Bacterial Degradation of Dental Polymeric Restorative Materials.
Ontology highlight
ABSTRACT:
SUBMITTER: Zhang N
PROVIDER: S-EPMC5459043 | biostudies-other | 2017 May
REPOSITORIES: biostudies-other
Similar Datasets
Project description:Polymeric materials are the first choice for restoring tooth cavities, bonding tooth-colored fillings, sealing root canal systems, and many other dental restorative applications. However, polymeric materials are highly susceptible to bacterial attachment and colonization, leading to dental diseases. Many approaches have been investigated to minimize the formation of biofilms over polymeric restorative materials and at the tooth/material interfaces. Among them, contact-killing compounds have shown promising results to inhibit dental biofilms. Contact-killing compounds can be immobilized within the polymer structure, delivering a long-lasting effect with no leaching or release, thus providing advantages compared to release-based materials. This review discusses cutting-edge research on the development of contact-killing compounds in dental restorative materials to target oral pathogens. Contact-killing compounds in resin composite restorations, dental adhesives, root canal sealers, denture-based materials, and crown cements have all demonstrated promising antibacterial properties. Contact-killing restorative materials have been found to effectively inhibit the growth and activities of several oral pathogens related to dental caries, periodontal diseases, endodontic, and fungal infections. Further laboratory optimization and clinical trials using translational models are needed to confirm the clinical applicability of this new generation of contact-killing dental restorative materials.
| S-EPMC7552663 | biostudies-literature
Project description:Oral biofilms attach onto both teeth surfaces and dental material surfaces in oral cavities. In the meantime, oral biofilms are not only the pathogenesis of dental caries and periodontitis, but also secondary caries and peri-implantitis, which would lead to the failure of clinical treatments. The material surfaces exposed to oral conditions can influence pellicle coating, initial bacterial adhesion, and biofilm formation, due to their specific physical and chemical characteristics. To define the effect of physical and chemical characteristics of dental prosthesis and restorative material on oral biofilms, we discuss resin-based composites, glass ionomer cements, amalgams, dental alloys, ceramic, and dental implant material surface properties. In conclusion, each particular chemical composition (organic matrix, inorganic filler, fluoride, and various metallic ions) can enhance or inhibit biofilm formation. Irregular topography and rough surfaces provide favorable interface for bacterial colonization, protecting bacteria against shear forces during their initial reversible binding and biofilm formation. Moreover, the surface free energy, hydrophobicity, and surface-coating techniques, also have a significant influence on oral biofilms. However, controversies still exist in the current research for the different methods and models applied. In addition, more in situ studies are needed to clarify the role and mechanism of each surface parameter on oral biofilm development.
| S-EPMC6213966 | biostudies-other
Project description:Resin-based composites are widely used as dental restorative materials due to their excellent properties. They must have high modulus, high hardness, and be chemically inert while minimizing moisture uptake. To fulfill these higher standard prerequisites and properties, continuous improvements in each of their components are required. This study develops novel composites with multiple biofunctions. Light-cured Bis-GMA/TEGDMA dental resin (RK)/layered double hydroxide intercalated with fluoride ions (LDH-F)/calcium bentonite (Bt) hybrid composites were prepared. The loading ratio of LDH-F to Bt was varied, ranging from 2.5/2.5 to 10/10 parts per hundred RK and structural, mechanical, and biological properties were studied. The incorporation of even small mass fractions (e.g., 2.5 wt % of LDH-F and 2.5 wt % of Bt) in RK dental resin significantly improved the mechanical properties of the pristine resin. The synthetized materials showed antibacterial and antibiofilm effects against three bacterial strains isolated from healthy volunteers' saliva (Streptococcus spp., Bacteroides fragilis, and Staphylococcus epidermidis) without affecting its ability to induce dental pulp stem cells differentiation into odontoblast-like cells. The capability to balance between the antibiofilm activity and dental pulp stem cells differentiation in addition with improved mechanical properties make these materials a promising strategy in preventive and restorative dentistry.
| S-EPMC7077377 | biostudies-literature
Project description:A great number of different types of materials have been used in dentistry as intermediate restoratives. Among them, new resin-based bases have been released in the dental market. The present study focuses on the identification of the organic eluates released from such materials and the study of their surface microstructure in combination with their corresponding elemental composition. For this purpose, the following materials were used:ACTIVA™BioACTIVE-BASE/LINER™, Ketac™Bond Glass Ionomer, SDR™ and Vitrebond™Light Cure Glass Ionomer Liner/Base. Methanolic leachates derived from polymerized materials were analyzed by means of gas chromatography-mass spectrometry (GC-MS). Scanning electron microscopy(SEM) was used for the surface monitoring of suitably prepared specimens. The GC-MS analysis revealed the elution of twenty different substances from the three resin-based materials, while none was eluted from the glass ionomer base. The SEM analysis for Vitrebond™ presented small pits, the one for Ketac™Bond presented elongated cracks, while no voids were present for ACTIVA™BioACTIVE-BASE/LINER™ and SDR™. Moreover, the resin matrix of some dental materials may inhibit elements' accumulation on the surface layers. Particularly, the detected organic eluents may be related to potential toxic effects.
| S-EPMC7180687 | biostudies-literature
Project description:Step-growth thiol-Michael photopolymerizable resins, constituting an alternative chemistry to the current methacrylate-based chain-growth polymerizations, were developed and evaluated for use as dental restorative materials. The beneficial features inherent to anion-mediated thiol-Michael polymerizations were explored, such as rapid photocuring, low stress generation, ester content tunability, and improved mechanical performance in a moist environment. An ester-free tetrafunctional thiol and a ultraviolet-sensitive photobase generator were implemented to facilitate thiol-Michael photopolymerization. Thiol-Michael resins of varied ester content were fabricated under suitable light activation. Polymerization kinetics and shrinkage stress were determined with Fourier-transform infrared spectroscopy coupled with tensometery measurements. Thermomechanical properties of new materials were evaluated by dynamic mechanical analysis and in 3-point bending stress-strain experiments. Photopolymerization kinetics, polymerization shrinkage stress, glass transition temperature, flexural modulus, flexural toughness, and water sorption/solubility were compared between different thiol-Michael systems and the BisGMA/TEGDMA control. Furthermore, the mechanical performance of 2 thiol-Michael composites and a control composite were compared before and after extensive conditioning in water. All photobase-catalyzed thiol-Michael polymerization matrices achieved >90% conversion with a dramatic reduction in shrinkage stress as compared with the unfilled dimethacrylate control. One prototype of ester-free thiol-Michael formulations had significantly better water uptake properties than the BisGMA/TEGDMA control system. Although exhibiting relatively lower Young's modulus and glass transition temperatures, highly uniform thiol-Michael materials achieved much higher toughness than the BisGMA/TEGDMA control. Moreover, low-ester thiol-Michael composite systems show stable mechanical performance even after extensive water treatment. Although further resin/curing methodology optimization is required, the photopolymerized thiol-Michael prototype resins can now be recognized as promising candidates for implementation in composite dental restorative materials.
| S-EPMC5958372 | biostudies-literature
Project description:This article contains data related to the research article titled "Compressive strength of glass ionomer and composite resin. In vitro study" (Blanco et al., 2017). The presented data gives information about the compressive strength of two restorative materials (Tetric N-Ceram® resin and Vitremer TM® resin) in class I cavities in birradicular premolars. The dental organs were subjected to a compressive vertical force at different deeps of cavities preparation until obtain fracture of the restorative material. Compression Resistance values of 380.5 are obtained; 387; 399.2; 419.9; 422.4; 428; 432.1 and 429 N for Tetric N-Ceram® and 349.4 resin; 350.2; 356.1; 369; 390.7; 416.2; 424 and 426.8 for the Vitremer TM® ionomer. There are significant statistical differences (p < 0.05) between restorative materials. The resin Tetric N-Ceram®, showed higher resistance to compression than Vitremer TM® resin in all depths.
| S-EPMC6660634 | biostudies-literature
Project description:BackgroundThe aim of this study was to investigate the influence of clinical characteristics and dental restorative materials on oral health-related quality of life in patients with oral lichen planus. In particular, the influences of amalgam and metals were investigated.MethodsA total of 112 patients with clinical and histological features of oral lichen planus from the Department of Cranio-Maxillofacial Surgery at the University Hospital of Münster participated in this prospective study. Clinical parameters of oral lichen planus and the dental restorative materials used were evaluated. Oral health-related quality of life was investigated by using the short form of the German version of the Oral Health Impact Profile (OHIP-14). In addition, physical pain was rated on a visual analogue scale.ResultsThe average OHIP-14 score was 13.54. A high correlation was seen between OHIP and pain. Likewise, higher OHIP-values were seen for male patients, and such as for those patients with non-reticular forms of oral lichen planus (OLP). A local form of OLP is more often seen on female patients, such as with the presence of reticular lichen. In regard to the restorations, the presence of composite restorations is correlated with a local lichen, whereas the presence of gold restorations is often seen with a generalized lichen. Furthermore, the grading of strength of association between mucosal lesion and amalgam/metal was tested. No significant differences revealed the analysis of the relationship between gender, clinical form of OLP, age, and presentation form between the 4 gradings of Thornhill.ConclusionsThe oral health-related quality of life is significantly limited in patients with oral lichen planus. But these OHIP scores are not influenced by the restorative materials. Here, pain severity is the most important aspect. We found no statistical differences in the clinical parameters between patients with amalgam or metal restoration and patients without these restorations. It is not necessary to replace amalgam fillings that are not in direct contact with mucosal surfaces.
| S-EPMC8126149 | biostudies-literature
Project description:ObjectivesTo test the hypotheses that (a) the chairside/handheld dental scanner combined with a metrology software will measure clinical wear in vivo in agreement with measurements from X-ray computed microtomography and; (b) polished monolithic zirconia does not cause accelerated wear of opposing enamel.Materials and methodsThirty single crowns were randomized to receive a monolithic zirconia or metal-ceramic crown. Two non-restored opposing teeth in the same quadrants were identified to serve as enamel controls. After cementation, quadrants were scanned using an intraoral dental scanner. Patients were recalled at 6-months and 1-year for re-scanning. Scanned images were compared using a metrology software to determine maximum vertical wear of teeth. The accuracy of the scanning measurements from this new method was compared with X-ray computed microtomography (micro-CT) measurements. Statistical analysis was performed using Mann-Whitney U test to determine significant differences between wear of enamel against zirconia, metal-ceramic or enamel. Linear regression analysis determined agreement between measurements obtained using intraoral scanning and micro-CT.ResultsRegression analysis demonstrated that there is a quantitative agreement between depth and volume measurements produced using intraoral scanning and the micro-CT methodologies. There was no significant difference between the wear of enamel against polished monolithic zirconia crowns and enamel against enamel.ConclusionsIntraoral scanning combined with a matching software can accurately quantify clinical wear to verify that monolithic zirconia exhibited comparable wear of enamel compared with metal-ceramic crowns and control enamel. Agreement between the intraoral scanner and the micro-CT was 99.8%. Clinical Trials.gov NCT02289781.
| S-EPMC7745065 | biostudies-literature
Project description:Tooth decay is prevalent, and secondary caries causes restoration failures, both of which are related to demineralization. There is an urgent need to develop new therapeutic materials with remineralization functions. This article represents the first review on the cutting edge research of poly(amido amine) (PAMAM) in combination with nanoparticles of amorphous calcium phosphate (NACP). PAMAM was excellent nucleation template, and could absorb calcium (Ca) and phosphate (P) ions via its functional groups to activate remineralization. NACP composite and adhesive showed acid-neutralization and Ca and P ion release capabilities. PAMAM+NACP together showed synergistic effects and produced triple benefits: excellent nucleation templates, superior acid-neutralization, and ions release. Therefore, the PAMAM+NACP strategy possessed much greater remineralization capacity than using PAMAM or NACP alone. PAMAM+NACP achieved dentin remineralization even in an acidic solution without any initial Ca and P ions. Besides, the long-term remineralization capability of PAMAM+NACP was established. After prolonged fluid challenge, the immersed PAMAM with the recharged NACP still induced effective dentin mineral regeneration. Furthermore, the hardness of pre-demineralized dentin was increased back to that of healthy dentin, indicating a complete remineralization. Therefore, the novel PAMAM+NACP approach is promising to provide long-term therapeutic effects including tooth remineralization, hardness increase, and caries-inhibition capabilities.
| S-EPMC6506538 | biostudies-literature
Project description:As the most advanced aerogel material, silica aerogel has had transformative industrial impacts. However, the use of silica aerogel is currently limited to the field of thermal insulation materials, so it is urgent to expand its application into other fields. In this work, silica aerogel/resin composites were successfully prepared by combining silica aerogel with a resin matrix for dental restoration. The applications of this material in the field of dental restoration, as well as its performance, are discussed in depth. It was demonstrated that, when the ratio of the resin matrix Bis-GMA to TEGDMA was 1:1, and the content of silica aerogel with 50 μm particle size was 12.5%, the composite achieved excellent mechanical properties. The flexural strength of the silica aerogel/resin composite reached 62.9546 MPa, which was more than five times that of the pure resin. Due to the presence of the silica aerogel, the composite also demonstrated outstanding antibacterial capabilities, meeting the demand for antimicrobial properties in dental materials. This work successfully investigated the prospect of using commercially available silica aerogels in dental restorative materials; we provide an easy method for using silica aerogels as dental restorative materials, as well as a reference for their application in the field of biomedical materials.
| S-EPMC9323775 | biostudies-literature