Bioactive Potential of 3D-Printed Oleo-Gum-Resin Disks: B. papyrifera, C. myrrha, and S. benzoin Loading Nanooxides-TiO2, P25, Cu2O, and MoO3.

ABSTRACT: This experimental study investigates the bioactive potential of filaments produced via hot melt extrusion (HME) and intended for fused deposition modeling (FDM) 3D printing purposes. The oleo-gum-resins from benzoin, myrrha, and olibanum in pure state and also charged with 10% of metal oxide nanoparticles, TiO2, P25, Cu2O, and MoO3, were characterized by ultraviolet-visible (UV-Vis) and Fourier transform infrared (FTIR) spectroscopy, energy-dispersive X-ray microanalysis (EDXMA), scanning electron microscopy (SEM), and differential scanning calorimetry (DSC). Disks were 3D-printed into model geometries (10 × 5 mm) and the disk-diffusion methodology was used for the evaluation of antimicrobial and antifungal activity of materials in study against the clinical isolates: Staphylococcus aureus, Pseudomonas aeruginosa, Escherichia coli, and Candida albicans. Due to their intrinsic properties, disks containing resins in pure state mostly prevent surface-associated growth; meanwhile, disks loaded with 10% oxides prevent planktonic growth of microorganisms in the susceptibility assay. The microscopy analysis showed that part of nanoparticles was encapsulated by the biopolymeric matrix of resins, in most cases remaining disorderly dispersed over the surface of resins. Thermal analysis shows that plant resins have peculiar characteristics, with a thermal behavior similar to commercial available semicrystalline polymers, although their structure consists of a mix of organic compounds.

SUBMITTER: Horst DJ

PROVIDER: S-EPMC5547715 | biostudies-other | 2017

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Sacraoxides A-G, Bioactive Cembranoids from Gum Resin of <i>Boswellia sacra</i>.

Project description:Seven undescribed cembranoids, sacraoxides A-G (1, 3-8) were isolated from the gum resin of Boswellia sacra. Their structures were elucidated by extensive physicochemical and spectroscopic analysis, as well as ECD calculation, modified Mosher's method and X-ray diffraction crystallography. Compounds 6 and 7 exhibited inhibitory activities on nitric oxide (NO) production induced by lipopolysaccharide in RAW264.7 cells with IC50 values of 24.9 ± 1.7 and 36.4 ± 2.9 μM.

| S-EPMC8044883 | biostudies-literature

Optical Approach to Resin Formulation for 3D Printed Microfluidics.

Project description:Microfluidics imposes different requirements on 3D printing compared to many applications because the critical features for microfluidics consist of internal microvoids. Resins for general 3D printing applications, however, are not necessarily formulated to meet the requirements of microfluidics and minimize the size of fabricated voids. In this paper we use an optical approach to guide custom formulation of resins to minimize the cross sectional size of fabricated flow channels as exemplars of such voids. We focus on stereolithgraphy (SL) 3D printing with Digital Light Processing (DLP) based on a micromirror array and use a commercially available 3D printer. We develop a mathematical model for the optical dose delivered through the thickness of a 3D printed part, including the effect of voids. We find that there is a fundamental trade-off between the homogeneity of the optical dose within individual layers and how far the critical dose penetrates into a flow channel during fabrication. We also experimentally investigate the practical limits of flow channel miniaturization given the optical properties of a resin and find that the minimum flow channel height is ~3.5-5.5ha where ha is the optical penetration depth of the resin, and that the minimum width is 4 pixels in the build plane. We also show that the ratio of the build layer thickness to ha should be in the range 0.3-1.0 to obtain the minimum flow channel height for a given resin. The minimum flow channel size that we demonstrate for a custom resin is 60 ?m × 108 ?m for a 10 ?m build layer thickness. This work lays the foundation for 3D printing of <100 ?m microfluidic features.

| S-EPMC4699590 | biostudies-literature

Bioactive Triterpenes of <i>Protium heptaphyllum</i> Gum Resin Extract Display Cholesterol-Lowering Potential.

Project description:Hypercholesterolemia is one of the major causes of cardiovascular disease, the risk of which is further increased if other forms of dyslipidemia occur. Current therapeutic strategies include changes in lifestyle coupled with drug administration. Statins represent the most common therapeutic approach, but they may be insufficient due to the onset of resistance mechanisms and side effects. Consequently, patients with mild hypercholesterolemia prefer the use of food supplements since these are perceived to be safer. Here, we investigate the phytochemical profile and cholesterol-lowering potential of Protium heptaphyllum gum resin extract (PHE). Chemical characterization via HPLC-APCI-HRMS2 and GC-FID/MS identified 13 compounds mainly belonging to ursane, oleanane, and tirucallane groups. Studies on human hepatocytes have revealed how PHE is able to reduce cholesterol production and regulate the expression of proteins involved in its metabolism. (HMGCR, PCSK9, LDLR, FXR, IDOL, and PPAR). Moreover, measuring the inhibitory activity of PHE against HMGR, moderate inhibition was recorded. Finally, molecular docking studies identified acidic tetra- and pentacyclic triterpenoids as the main compounds responsible for this action. In conclusion, our study demonstrates how PHE may be a useful alternative to contrast hypercholesterolemia, highlighting its potential as a sustainable multitarget natural extract for the nutraceutical industry that is rapidly gaining acceptance as a source of health-promoting compounds.

| S-EPMC7961947 | biostudies-literature

TiO2@Cu2O n-n Type Heterostructures for Photochemistry.

Project description:A TiO2@Cu2O semiconductor heterostructure with better photochemical response compared to TiO2 was obtained using an electrochemical deposition method of Cu2O on the surface of TiO2 nanotubes. The choice of 1D nanotubes was motivated by the possibility of achieving fast charge transfer, which is considered best suited for photochemical applications. The morphology and structural properties of the obtained heterojunction were determined using standard methods -SEM and Raman spectroscopy. Analysis of photoelectrochemical properties showed that TiO2@Cu2O heterostructures exhibit better properties resulting from an interaction with sunlight than TiO2. A close relationship between the morphology of the heterostructures and their photoproperties was also demonstrated. Investigations representing a combination of photoelectrochemical cells for hydrogen production and photocatalysis-photoelectrocatalysis-were also carried out and confirmed the observations on the photoproperties of heterostructures. Analysis of the Mott-Schottky plots as well as photoelectrochemical measurements (Iph-V, Iph-t) showed that TiO2 as well as, unusually, Cu2O exhibit n-type conductivity. On this basis, a new energy diagram of the TiO2@Cu2O system was proposed. It was found that TiO2@Cu2O n-n type heterostructure prevents the processes of photocorrosion of copper(I) oxide contained in a TiO2-based heterostructure.

| S-EPMC8269846 | biostudies-literature

Mechanical Properties of 3D-Printed Acrylonitrile-Butadiene-Styrene TiO2 and ATO Nanocomposites.

Project description:In order to enhance the mechanical performance of three-dimensional (3D) printed structures fabricated via commercially available fused filament fabrication (FFF) 3D printers, novel nanocomposite filaments were produced herein following a melt mixing process, and further 3D printed and characterized. Titanium Dioxide (TiO2) and Antimony (Sb) doped Tin Oxide (SnO2) nanoparticles (NPs), hereafter denoted as ATO, were selected as fillers for a polymeric acrylonitrile butadiene styrene (ABS) thermoplastic matrix at various weight % (wt%) concentrations. Tensile and flexural test specimens were 3D printed, according to international standards. It was proven that TiO2 filler enhanced the overall tensile strength by 7%, the flexure strength by 12%, and the micro-hardness by 6%, while for the ATO filler, the corresponding values were 9%, 13%, and 6% respectively, compared to unfilled ABS. Atomic force microscopy (AFM) revealed the size of TiO2 (40 ± 10 nm) and ATO (52 ± 11 nm) NPs. Raman spectroscopy was performed for the TiO2 and ATO NPs as well as for the 3D printed nanocomposites to verify the polymer structure and the incorporated TiO2 and ATO nanocrystallites in the polymer matrix. The scope of this work was to fabricate novel nanocomposite filaments using commercially available materials with enhanced overall mechanical properties that industry can benefit from.

| S-EPMC7407130 | biostudies-literature

Novel carbon-fiber microelectrode batch fabrication using a 3D-printed mold and polyimide resin.

Project description:Glass insulated carbon-fiber microelectrodes (CFMEs) are standard tools for the measurement of neurotransmitters. However, electrodes are fabricated individually and the glass can shatter, limiting application in higher order mammals. Here, we developed a novel microelectrode batch fabrication method using a 3D-printed mold and polyimide resin insulating agent. The 3D-printed mold is low cost, customizable to change the electrode shape, and allows 40 electrodes to be made simultaneously. The polyimide resin is biocompatible, quick to cure, and does not adhere to the plastic mold. The electrodes were tested for the response to dopamine with fast-scan cyclic voltammetry both in vitro and in vivo and performed similarly to traditional glass-insulated electrodes, but with lower background currents. Thus, polyimide-insulated electrodes can be mass-produced using a 3D-printed mold and are an attractive alternative for making cheap, biocompatible microelectrodes.

| S-EPMC5019535 | biostudies-literature

A Bioactive Hydrogel and 3D Printed Polycaprolactone System for Bone Tissue Engineering.

Project description:In this study, a hybrid system consisting of 3D printed polycaprolactone (PCL) filled with hydrogel was developed as an application for reconstruction of long bone defects, which are innately difficult to repair due to large missing segments of bone. A 3D printed gyroid scaffold of PCL allowed a larger amount of hydrogel to be loaded within the scaffolds as compared to 3D printed mesh and honeycomb scaffolds of similar volumes and strut thicknesses. The hydrogel was a mixture of alginate, gelatin, and nano-hydroxyapatite, infiltrated with human mesenchymal stem cells (hMSC) to enhance the osteoconductivity and biocompatibility of the system. Adhesion and viability of hMSC in the PCL/hydrogel system confirmed its cytocompatibility. Biomineralization tests in simulated body fluid (SBF) showed the nucleation and growth of apatite crystals, which confirmed the bioactivity of the PCL/hydrogel system. Moreover, dissolution studies, in SBF revealed a sustained dissolution of the hydrogel with time. Overall, the present study provides a new approach in bone tissue engineering to repair bone defects with a bioactive hybrid system consisting of a polymeric scaffold, hydrogel, and hMSC.

| S-EPMC5770986 | biostudies-literature

The Effect of Binder Loading on the Pore Size of 3D Printed PMMA.

Project description:Binder jetting is known to produce porous objects by depositing the binder selectively layer by layer on a powder bed. In this study, the pore size of printed parts and the correlating mechanical properties are investigated on a commercially available PMMA powder binder system. Pore sizes are measured via capillary flow porometry and mechanical properties via tensile tests. Porometry indicates that the pore size stays at a constant level of 22 µm at 5 to 10 wt% binder loading before decreasing to 6 µm at loadings of 30 wt% or higher. The results were compared with the mechanical testing and related to the agglomerate strength model of Rumpf. The highlights of the article are the application of a binder jetted part as a filter and the identification of a close relationship between porosity and mechanical strength, similar to phenomena in agglomeration science.

| S-EPMC7959472 | biostudies-literature

Advancing 3D-Printed Microfluidics: Characterization of a Gas-Permeable, High-Resolution PDMS Resin for Stereolithography.

Project description:The rapid expansion of microfluidic applications in the last decade has been curtailed by slow, laborious microfabrication techniques. Recently, microfluidics has been explored with additive manufacturing (AM), as it has gained legitimacy for producing end-use products and 3D printers have improved resolution capabilities. While AM satisfies many shortcomings with current microfabrication techniques, there still lacks a suitable replacement for the most used material in microfluidic devices, poly(dimethylsiloxane) (PDMS). Formulation of a gas-permeable, high-resolution PDMS resin was developed using a methacrylate-PDMS copolymer and the novel combination of a photoabsorber, Sudan I, and photosensitizer, 2-Isopropylthioxanthone. Resin characterization and 3D printing were performed using a commercially available DLP-SLA system. A previously developed math model, mechanical testing, optical transmission, and gas-permeability testing were performed to validate the optimized resin formula. The resulting resin has Young's modulus of 11.5 MPa, a 12% elongation at break, and optical transmission of >75% for wavelengths between 500 and 800 nm after polymerization, and is capable of creating channels as small as 60 μm in height and membranes as thin as 20 μm. The potential of AM is just being realized as a fabrication technique for microfluidics as developments in material science and 3D printing technologies continue to push the resolution capabilities of these systems.

| S-EPMC8540252 | biostudies-literature

The chemical, mechanical, and physical properties of 3D printed materials composed of TiO2-ABS nanocomposites.

Project description:To expand the chemical capabilities of 3D printed structures generated from commercial thermoplastic printers, we have produced and printed polymer filaments that contain inorganic nanoparticles. TiO2 was dispersed into acrylonitrile butadiene styrene (ABS) and extruded into filaments with 1.75 mm diameters. We produced filaments with TiO2 compositions of 1%, 5%, and 10% (kg/kg) and printed structures using a commercial 3D printer. Our experiments suggest that ABS undergoes minor degradation in the presence of TiO2 during the different processing steps. The measured mechanical properties (strain and Young's modulus) for all of the composites are similar to those of structures printed from the pure polymer. TiO2 incorporation at 1% negatively affects the stress at breaking point and the flexural stress. Structures produced from the 5 and 10% nanocomposites display a higher breaking point stress than those printed from the pure polymer. TiO2 within the printed matrix was able to quench the intrinsic fluorescence of the polymer. TiO2 was also able to photocatalyze the degradation of a rhodamine 6G in solution. These experiments display chemical reactivity in nanocomposites that are printed using commercial 3D printers, and we expect that our methodology will help to inform others who seek to incorporate catalytic nanoparticles in 3D printed structures.

| S-EPMC4929622 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data