Structurally Diverse Nitric Oxide-Releasing Poly(propylene Imine) Dendrimers.

ABSTRACT: Structurally diverse secondary amine-functionalized poly(propylene imine) (PPI) dendrimers capable of tunable nitric oxide (NO) release were synthesized in a straightforward, one-step manner using ring-opening or conjugate-addition reactions with propylene oxide (PO), styrene oxide (SO), acrylonitrile (ACN), poly(ethylene glycol) methyl ether acrylate (average Mn = 480) (PEG) or 1,2-epoxy-9-decene (ED). N-Diazeniumdiolate nitric oxide donors were formed on the resulting secondary amine-functionalized G2-G5 PPI dendrimers by reaction with NO gas in basic solution. The NO storage and release kinetics for the resulting dendritic scaffolds were diverse (0.9-3.8 ?mol NO/mg totals and 0.3 to 4.9 h half lives), illustrating the importance of the exterior chemical modification (e.g., steric environments, hydrophobicity, etc.) on diazeniumdiolate stability/decomposition. Tunable NO release was demonstrated by combining two donor systems on the exterior of one macromolecular scaffold. Additionally, a mathematical model was developed that allows for the simulation of dual NO release kinetics using the NO release data from the two single NO donor systems. The approaches described herein extend the range and scope of NO-releasing macromolecular scaffolds by unlocking a series of materials for use as dopants in biomedical polymers or stand-alone therapeutics depending on the exterior modification.

SUBMITTER: Lu Y

PROVIDER: S-EPMC3204868 | biostudies-literature | 2011 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Structurally Diverse Nitric Oxide-Releasing Poly(propylene Imine) Dendrimers.

Lu Yuan Y Sun Bin B Li Chenghong C Schoenfisch Mark H MH

Chemistry of materials : a publication of the American Chemical Society 20110901 18

Structurally diverse secondary amine-functionalized poly(propylene imine) (PPI) dendrimers capable of tunable nitric oxide (NO) release were synthesized in a straightforward, one-step manner using ring-opening or conjugate-addition reactions with propylene oxide (PO), styrene oxide (SO), acrylonitrile (ACN), poly(ethylene glycol) methyl ether acrylate (average Mn = 480) (PEG) or 1,2-epoxy-9-decene (ED). N-Diazeniumdiolate nitric oxide donors were formed on the resulting secondary amine-functiona ...[more]

PMID: 22053127

Similar Datasets

Project description:Nitric oxide (NO) releasing polymers have been widely applied as biomaterials for a variety of biomedical implants and devices. However, the chemical leaching of NO donors and their byproduct species is almost always observed during the application of polymers doped with NO donors, unless the donor is covalently linked to the polymer. Herein, we report the first NO releasing poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) fluorinated copolymer prepared by incorporating a fluorinated S-nitrosothiol as the NO donor. Under physiological conditions, the resulting polymeric films can release NO for 16?days. Importantly, due to both fluorine-fluorine and electrostatic charge interactions between the fluorinated NO donor and the PVDF-HFP copolymer, the total chemical leaching of the fluorinated NO donor and its disulfide product after 9?day was only 0.6% (mol%) of the initial amount of NO donor loaded into the film. These new NO release PVDF-HFP films exhibit antimicrobial and anti-biofilm activities against both Gram positive S. aureus and Gram negative P. aeruginosa strains. The NO-releasing PVDF-HFP polymer can also be coated on Teflon tubing to release NO under physiological conditions for extended time periods. This NO-releasing PVDF-HFP copolymer with greatly reduced chemical leaching could help enhance the biocompatibility and antimicrobial activity of various biomedical devices. STATEMENT OF SIGNIFICANCE: Fluoropolymers have been widely used in creating various biomedical implants and devices. However, nitric oxide (NO) release fluoropolymers have not been well studied to date. Additionally, in the application of biomaterials doped with NO donors, a significant amount of NO donors and their byproducts almost always leach into aqueous environment. We now report an NO releasing poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) fluoropolymer by incorporating a new fluorinated S-nitrosothiol. The NO release can last for 16?days under physiological conditions. The total chemical leaching was determined to be only 0.6?mol% of the initial S-nitrosothiol loaded. As expected, significant antimicrobial/anti-biofilm activities of the NO release PVDF-HFP film were observed against Gram positive S. aureus and Gram negative P. aeruginosa bacterial strains.

Dataset Information

Structurally Diverse Nitric Oxide-Releasing Poly(propylene Imine) Dendrimers.

Publications

Structurally Diverse Nitric Oxide-Releasing Poly(propylene Imine) Dendrimers.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets